hygrothermal ageing
Effects of hygrothermal ageing and thermal shock on reliability of interfacial adhesion between black oxide coated copper substr
      
The reliability of adhesion performance of the coating was evaluated before and after accelerated hygrothermal ageing, such as temperature cycling, pressure cooker test, and moisture sensitivity test followed by thermal shock.
      
The interfacial adhesion with a polyimide adhesive tape and an epoxy moulding compound was measured using the button shear and tape peel tests after hygrothermal ageing in an autoclave, high temperature ageing and thermal cycles.
      
Hygrothermal ageing at 121°C/100% RH in an autoclave was most detrimental to adhesion performance because of the combined effect of elevated temperature and high humidity.
      
Hygrothermal ageing and fracture of glass fibre-epoxy composites
      
The effects of hygrothermal ageing upon the failure characteristics and work of fracture of glass fibres in epoxy are described.
      
This information is combined with models of fracture in the construction of a fracture map which is used to interpret hygrothermal ageing phenomena.
      
Large decreases in shear strength were found on hygrothermal ageing, but reversed completely by slow, careful drying.
      
Electrical investigation improved the understanding of the hygrothermal ageing phenomena.
      
The influence of water uptake due to the hygrothermal ageing (HA) process on residual fracture performance was also studied.
      
Ultrasonic spectroscopy can be used to detect the damage caused to fibre-reinforced polymer materials due to hygrothermal ageing.
      
 