dispersion capacity
The dispersion capacity values of CuO measured by the two methods are consistent, which are of 1.20 mmol CuO/100 m2 CeO2.
      
1The dispersion capacity of MoO3 supported on CeO2 is 0.81 rnmo1/100 m2.
      
The dispersion capacity of MoO3 on the surface of α-Fe2O3 determined by XRD and XPS was 0.8 mmol/100m2 α-Fe2O3 in the samples calcined at 420°C.
      
Slurry prepared MoO3/γ-Al2O3 catalyst exhibited higher activity and dispersion capacity than conventional one.
      
Slurry prepared MoO>amp;lt;Subscript>amp;gt;3>amp;lt;/Subscript>amp;gt;/>amp;amp;ggr;-Al>amp;lt;Subscript>amp;gt;2>amp;lt;/Subscript>amp;gt;O>amp;lt;Subscript>amp;gt;3>amp;lt;/Subscript>amp;gt; catalyst exhibited higher activity and dispersion capacity than conventional one.
      
(2) Comparisons of the coefficient of variation of metal content values in 'town' versus 'village' furnished indications on the dispersion capacity of the metal particles.
      
There is a threshold monolayer dispersion capacity.
      
Monolayer dispersion capacity obtained by quantitative XRD phase analysis and M?ssbauer spectra analysis are consistent with each other, having the same value of 0.052 g Fe2O3/100 m2 α-Al2O3 surface.
      
Phase analysis by XRD measurements demonstrated that there was a threshold value in the indium content, i.e., the maximum dispersion capacity of indium oxides.
      
All the results collected seem basically consistent with a value of about 2.5-3 atomCu nm-2 for the maximum dispersion capacity of CuO on the ETS-10 matrix.
      
Silica-supported MoO3 catalyst prepared by slurry impregnation method exhibits higher activity and dispersion capacity compared to the MoO3/SiO2 prepared conventionally.
      
Monolayer dispersion capacity of CeO2 on the surface of the CeO2/MgAl2O4 catalyst and its effect on the De-SO2 activity
      
In contrast, the 24h SC treated sample showed an enhanced dispersion capacity with respect to the untreated sample.
      
This is due to its high dispersion capacity, which permits to deflocculate even very small particle clusters.
      
The point of intersection of the two lines can be regarded as a threshold corresponding to the monolayer dispersion capacity.
      
With the increase of the WO3 loading, especially beyond the monolayer dispersion capacity, a band at 202 cm21 becomes pronounced.
      
 