alumina spinel
    Development and application of alumina spinel castable for LF refining ladle
    LF精炼钢包用铝尖晶石浇注料的研制与应用
    6) Corrosion mechanism of alumina spinel self-flow castables was analyzed according to the phase diagram,the main reason of slag penetration is the increases of Fe2O3 in slag or low melting point phase CF.
    6)对于转炉末期渣,随着水泥含量增加,浇注料的抗渗透性增强,抗熔蚀性变差; 7)应用相图分析了铝尖晶石浇注料的侵蚀机理,认为渣中Fe_2O_3或低熔点相CF的增加是渣渗透的主要原因。
    Development and application of high alumina spinel carbon brick
    高铝尖晶石炭砖的研制及使用
    Special grade banxite grog of Yangquan. fused magnesia-alumina spinel clinker and flake graphite were used as starting material and phenolic resin as binder to produce high alumina spinel carbon brick, which showed good high temperature performance and good resistance to slag corrosion and thermal shock when used in a 100 ton ladle(open hearth furnace)the brick had 40%~70% residual thickness after being served for 70 heats.
    以阳泉特级高铝料、电熔镁铝尖晶石砂、鳞片状石墨为原料,以酚醛树脂为结合剂试制的高铝尖晶石炭砖,高温性能好,抗渣性强,耐热冲击性能好。 在100t炼钢平炉钢包上使用,寿命达70次以上,残砖厚度仍有40%~70%。
    The effect of alumina enriched magnesia alumina spinel on slag resistance and Ca treated steel resistance of magnesia refractories was investigated.
    研究了富铝尖晶石对镁质耐火材料抗钢渣与抗钙处理钢侵蚀性的影响。
    The investigation has shown:1)With the increasing of alumina enriched magnesia alumina spinel in the matrix,the resistance to basic slag penetration tends to increase,while the resistances to basic slag corrosion and Ca treated steel tend to decrease;
    结果表明 :随着富铝尖晶石加入量的增加 ,镁质耐火材料的抗钙处理钢和钢渣熔蚀性逐渐减弱 ,而抗钢渣渗透性逐渐增强 ;
 