钙云母
相关语句
  ca-mica
     The crystallization of Ca-mica in the CaO-MgO-Al2O3-SiO2-F system was studied in this paper.
     本文研究了钙云母在CaO-MgO-Al2O3-SiO2-F系玻璃基体中的生长过程。
短句来源
     Study on High Strength Dental Machinable Glass-ceramics Mainly-containing Ca-mica
     以钙云母为主相的高强度可切削牙科微晶玻璃的研究
短句来源
     The study on microstructure and properties of glass ceramics containing Ca- mica
     以钙云母为主相的可切削微晶玻璃的显微结构和性能
短句来源
     The study on preparation process, microstructure, strengthening and toughening mechanisms of MGC mainly containing Ca-mica were investigated, together with mechanical properties, machinability, and preliminary biological evaluation.
     本研究对以钙云母为主相的可切削微晶玻璃的制备工艺、结构特点、增强增韧机理及力学性能、加工性能和初步的生物学性能进行了较系统的研究。
短句来源
     The study on preparation process, microstructure, strengthening and toughening mechanisms of MGC mainly containing Ca-mica were investigated, together with mechanical properties and machinability.
     本研究对以钙云母为主相的可切削微晶玻璃的制备工艺、结构特点、增强增韧机理及力学性能等进行了初步的研究。
短句来源
更多       
  calcium mica
     In this study , according to the design of increasing bonding strength between interlayers, phlogopite type calcium mica glass ceramic has been developed .
     研究根据提高云母层间结合强度的构想 ,研制以钙云母为主相可切削微晶玻璃。
短句来源
     Objective In terms of the problems of now available dental machinable ceramics, a new type of calcium mica glass ceramic, PMC Ⅰ ceramic, was developed, and its machinability was compared with that of Vita MKII quantitatively. Moreover, the relationship between the strength and the machinability of PMC Ⅰ ceramic was studied.
     目的 对作者研制的一种新型含钙云母玻璃陶瓷PMC Ⅰ型陶瓷的可切削性能与VitaMKⅡ陶瓷进行定量比较 ,探讨PMC Ⅰ型陶瓷强度与其可切削性的关系。
短句来源
     Objective To study the strengthening of fluorophlogopite based dental machinable ceramic through developing a new type of calcium mica based ceramic.
     目的 研制一种新型的钙云母增强陶瓷 ,探讨提高氟金云母类切削陶瓷材料强度的方法。
短句来源
     Results A new type of calcium mica based glass ceramic was developed and had the 3 point bending strength of (210 2±14 7)MPa. Compared with the strength of fluorophlogopite based dental machinable ceramic,such as Dicor MGC, which was reported in the range of 150~180 MPa within inclusive studies,the higher strength of the new ceramic was recorded.
     结果 得到了钙云母增强的新型切削陶瓷 ,其三点抗弯强度达到 (2 10 2±14 7)MPa。
短句来源
  “钙云母”译为未确定词的双语例句
     the highest bending strength is 235MPa and the corresponding toughness is 2.17 MPa.
     按材料特点设计组成,采用二步法热处理,制得了以钙云母为主相的微晶玻璃,强度高达235MPa,断裂韧性最高2.17Mpa.
短句来源
     In CaO-MgO-Al_2O_3-SiO_2-F system, the effect of microstructure of the new-type fluorophlogopite-Ca machinable glass-ceramic on its properties was investigated.
     在CaO-MgO-Al_2O_3 -SiO_2 -F系新型钙云母可切削玻璃陶瓷体系中,研究分析了不同显微结构对性能的影响。
短句来源
     The glass-ceramics containing large-number less crystals showed higher strength.
     含有大量细小板条形钙云母晶体的微晶玻璃,强度较高。
短句来源
     K+ promoted mica's basic unit [AlSiO3] to form zirconia provided nucleating site for planar like mica crystal.
     K~+促进了云母相基本基团[AlSiO_3]的形成。 实验证明钙云母晶体的生长过程受界面跃迁过程控制。
短句来源
     The strength of machinable glass ceramics mainly containing Ca phlogopite and zirconia is 184MPa, fracture toughness is 2.17MPa·m 1/2 ,which are much more one times than VITA, a kind of commercial medical machinable glass ceramics . The machinablity is good .
     以钙云母和氧化锆为主相的微晶玻璃 ,具有棒状、长径比大、相互交错的晶粒 ; 强度 184MPa ,断裂韧性 2 .17MPa·m1/ 2 ,比目前临床用VITA提高了一倍 ,切削性能优良 ;
短句来源
更多       
查询“钙云母”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  ca-mica
In the K2O-CaO-MgO-Al2O3-SiO2-F system, a new-type glass-ceramic containing fluorophlogopite Ca-mica has been synthesized.
      


In this study , according to the design of increasing bonding strength between interlayers, phlogopite type calcium mica glass ceramic has been developed .The strength of machinable glass ceramics mainly containing Ca phlogopite and zirconia is 184MPa, fracture toughness is 2.17MPa·m 1/2 ,which are much more one times than VITA, a kind of commercial medical machinable glass ceramics .The machinablity is good .SEM shows, mica crystals are rod shaped, with larger aspect ratio than 10 and interlocking....

In this study , according to the design of increasing bonding strength between interlayers, phlogopite type calcium mica glass ceramic has been developed .The strength of machinable glass ceramics mainly containing Ca phlogopite and zirconia is 184MPa, fracture toughness is 2.17MPa·m 1/2 ,which are much more one times than VITA, a kind of commercial medical machinable glass ceramics .The machinablity is good .SEM shows, mica crystals are rod shaped, with larger aspect ratio than 10 and interlocking. The section plane of rupture and machining fracture mainly are cleavage and like cleavage fracture between mica layers, therefore smooth surface were made during machining and tolerance is easily realized. The feature of fracture illuminates intrinsically reinforcement is increasing bond strength between interlayers.

研究根据提高云母层间结合强度的构想 ,研制以钙云母为主相可切削微晶玻璃。以钙云母和氧化锆为主相的微晶玻璃 ,具有棒状、长径比大、相互交错的晶粒 ;强度 184MPa ,断裂韧性 2 .17MPa·m1/ 2 ,比目前临床用VITA提高了一倍 ,切削性能优良 ;材料的断裂和加工断口主要是云母层间的解理断裂和准解理断裂 ;故切削面光滑 ,易于保证加工的精度。同时说明提高云母层间结合强度是此类材料增强的本质所在

Objective In terms of the problems of now available dental machinable ceramics, a new type of calcium mica glass ceramic, PMC Ⅰ ceramic, was developed, and its machinability was compared with that of Vita MKII quantitatively. Moreover, the relationship between the strength and the machinability of PMC Ⅰ ceramic was studied. Methods Samples of PMC Ⅰ ceramic were divided into four groups according to their nucleation procedures. 600 seconds drilling tests were conducted with high speed steel tools(Φ=2...

Objective In terms of the problems of now available dental machinable ceramics, a new type of calcium mica glass ceramic, PMC Ⅰ ceramic, was developed, and its machinability was compared with that of Vita MKII quantitatively. Moreover, the relationship between the strength and the machinability of PMC Ⅰ ceramic was studied. Methods Samples of PMC Ⅰ ceramic were divided into four groups according to their nucleation procedures. 600 seconds drilling tests were conducted with high speed steel tools(Φ=2 3 mm) to measure the drilling depths of Vita MKII ceramic and PMC Ⅰ ceramic, while constant drilling speed of 600 rpm and constant axial load of 39 2 N were used. And the 3 point bending strength of the four groups of PMC Ⅰ ceramic were recorded.Results Drilling depth of Vita MKII was 0 71 mm, while the depths of the four groups of PMC Ⅰ ceramic were 0 88 mm?1 40 mm?0.40 mm and 0 90 mm, respectively. Group B of PMC Ⅰ ceramic showed the largest depth of 1 40 mm and was statistically different from other groups and Vita MKII. And the strength of the four groups of PMC Ⅰ ceramic were 137 7?210 2?118 0 and 106 0 MPa, respectively.Conclusion The machinability of the new developed dental machinable ceramic of PMC Ⅰ could meet the need of the clinic.

目的 对作者研制的一种新型含钙云母玻璃陶瓷PMC Ⅰ型陶瓷的可切削性能与VitaMKⅡ陶瓷进行定量比较 ,探讨PMC Ⅰ型陶瓷强度与其可切削性的关系。方法 采用钻孔实验方法 ,测定A、B、C、D4组不同晶化处理的PMC Ⅰ型陶瓷及VitaMKⅡ陶瓷材料 60 0s的钻孔深度 ,同时测定4组PMC Ⅰ型陶瓷的 3点抗弯强度。结果 VitaMKⅡ的钻孔深度为 0 71mm ;4组PMC Ⅰ型陶瓷的钻孔深度分别为 0 88mm、1 40mm、0 40mm和 0 90mm。其中 ,B组样品与其余组别及VitaMKⅡ陶瓷的差异有显著性 (P <0 0 5)。 4组PMC Ⅰ型陶瓷的 3点抗弯强度分别为 1 37 7、2 1 0 2、1 1 8 0和 1 0 6 0MPa。结论 新型PMC Ⅰ型切削陶瓷的可切削性已能够满足临床要求

To develop a new type of high strength calcium mica containing dental machinable ceramic Materials compositions were selected and glass ceramics were obtained through the treatment of glass preparation and nucleation Then crystal contents of glass ceramics were analysed by X ray diffraction analysis (XRD) and the 3 point bending strength of the new ceramic were recorded A new type of calcium mica containing glass ceramic was developed and its 3 point bending strength of (210 2±14 7) MPa was...

To develop a new type of high strength calcium mica containing dental machinable ceramic Materials compositions were selected and glass ceramics were obtained through the treatment of glass preparation and nucleation Then crystal contents of glass ceramics were analysed by X ray diffraction analysis (XRD) and the 3 point bending strength of the new ceramic were recorded A new type of calcium mica containing glass ceramic was developed and its 3 point bending strength of (210 2±14 7) MPa was recorded [Conclusion] The new type of high strength dental machinable ceramic can be obtained by means of the modification of the crystal structure of phlogopite glass ceramic

【目的】研制一种新型的高强度钙云母牙科切削陶瓷材料。【方法】筛选材料配方 ,通过玻璃熔制、晶化热处理 ,得到玻璃陶瓷 ,用X射线衍射分析玻璃陶瓷的晶相成分 ,并用三点抗弯法测量材料的强度。【结果】得到了含钙云母的新型切削陶瓷 ,其三点抗弯强度最高达到 (2 10 2± 14 7)MPa。【结论】通过改变金云母玻璃陶瓷内部的晶体结构可以得到新型具有较高强度的牙科切削陶瓷。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关钙云母的内容
在知识搜索中查有关钙云母的内容
在数字搜索中查有关钙云母的内容
在概念知识元中查有关钙云母的内容
在学术趋势中查有关钙云母的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社