酸性水罐 sour water tank(7) acidic water container(3)   sour water tank      The corrosion of the sour water tank V6203 in heavy oil FCC unit mainly was the uniform corrosion and stress corrosion cracking caused by H2S. The pits of under-deposit corrosion were the sources of stress corrosion cracking.      重油催化装置酸性水罐V6 2 0 3的腐蚀主要是H2 S引起的均匀腐蚀和应力腐蚀开裂 ,而垢下腐蚀形成的蚀坑则是应力腐蚀开裂的裂纹源。 短句来源      The problem of serious stress corrosion existed in sour water tank in sour water striping unit of sulphur workshop was analyzed.      对硫磺车间的酸性水汽提装置中的酸性水罐存在的严重应力腐蚀问题进行了分析。 短句来源      CLOSED DEODORIZATION IN THE SOUR WATER TANK OF SOUR STRIPPING UNIT      污水汽提酸性水罐密闭除臭 短句来源      The sour water tank in the stripping unit normally has a dome roof, a great quantity of pungent odorizing gas containing ammonia diffusing from the top of the tank, which pollutes environment and impact on the human health.      污水汽提装置酸性水罐一般为拱顶罐,罐顶散发大量含硫、含氨等恶臭气体,污染周围环境和影响人体健康。 短句来源      Corrosion of Sour Water Tank in Heavy Oil FCCU      重油催化酸性水罐的腐蚀 短句来源 更多          acidic water container      Application of Nano Titanium Polymer Paint in Acidic Water Container      钛纳米聚合物涂料在酸性水罐的应用 短句来源      Application of nano titanium polymer paint in acidic water container      钛纳米聚合物涂料在酸性水罐上的应用 短句来源      Stress corrosion of acidic water container in sulfur workshop was analyzed.      本文对硫磺车间的酸性水气体装置中的酸性水罐存在的严重应力腐蚀问题进行分析。 对防腐涂料进行了试验筛选,确定采用钛纳米聚合物涂料作防腐涂层。 短句来源   “酸性水罐”译为未确定词的双语例句      When it was used in the 3 sour water tanks i.e. V108, V206 and V106/1 in sulfur manufacturing workshop, the tanks have been operating for more than 2 years without any problems.      经在制硫车间V10 8,V2 0 6和V10 6 /1三个酸性水罐工业应用 ,至今已运行两年多 ,涂层仍完好。 短句来源      Stress corrosion of aci dic wate r container in sulfur workshop was analy zed.      对硫磺车间的酸性水气体装置中的酸性水罐存在的严重的应力腐蚀问题进行分析。 短句来源 查询“酸性水罐”译词为用户自定义的双语例句     我想查看译文中含有：的双语例句 为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法，我们为您准备了出自英文原文的大量英语例句，供您参考。          The corrosion of the sour water tank V6203 in heavy oil FCC unit mainly was the uniform corrosion and stress corrosion cracking caused by H2S. The pits of under-deposit corrosion were the sources of stress corrosion cracking. After being protected by glass scale coating, the tank has been operating smoothly for more than 3 years.             重油催化装置酸性水罐V6 2 0 3的腐蚀主要是H2 S引起的均匀腐蚀和应力腐蚀开裂 ,而垢下腐蚀形成的蚀坑则是应力腐蚀开裂的裂纹源。经采用玻璃鳞片涂料进行防护后 ,已运行 3年 ,至今仍完好。 文摘来源          The performances and application of W2-1 type vinyl ester epoxy and its glass flake coating were introduced. The coating which had excellent anti-corrosion and anti-permeation performances could be used in organic acid, inorganic acid, alkaline, salt and sea water environments and the long-term service temperature was as high as 100℃. When it was used in the 3 sour water tanks i.e. V108, V206 and V106/1 in sulfur manufacturing workshop, the tanks have been operating for more than 2 years without any proble...             介绍了W2 - 1型乙烯基酯树脂及其玻璃鳞片重防腐蚀涂料的性能及应用情况 ,指出该涂料具有优异的耐蚀抗渗性能 ,可用于多种无机酸、有机酸、碱、盐和海水等环境 ,长期使用温度可达 10 0℃。经在制硫车间V10 8,V2 0 6和V10 6 /1三个酸性水罐工业应用 ,至今已运行两年多 ,涂层仍完好。为提高其耐碱性 ,可在表面增涂一层树脂面漆。 文摘来源          Stress corrosion of aci dic wate r container in sulfur workshop was analy zed.Experiments were done to choose the best anti-corrosive paint.Nano titanium polymer paint was chosen as the anticor rosive paint.After application for one y ear,the service life of the acidic water container has been proved to be prolong ed.             对硫磺车间的酸性水气体装置中的酸性水罐存在的严重的应力腐蚀问题进行分析。对防腐涂料进行了筛选 ,确定采用钛钠米聚合物涂料作防腐涂层。通过 1年的使用证明其达到了提高酸性水罐使用寿命的目的。 文摘来源   << 更多相关文摘         相关查询: 酸性 水罐 酸性脂肪酶 粪水罐 酸性油 水罐挂车 酸性紫 酸性胶体 酸性脂酶 酸性腐殖化作用 酸性饲料 酸性氧化物  对查询结果不满意

CNKI小工具 在Springer中查有关的英文论文 在知识搜索中查有关酸性水罐的内容 在数字搜索中查有关酸性水罐的内容 在概念知识元中查有关酸性水罐的内容 在学术趋势中查有关酸性水罐 的内容

CNKI主页 |  设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务

2008 CNKI－中国知网

京ICP证040431号 互联网出版许可证 新出网证(京)字008号 北京市公安局海淀分局 备案号：110 1081725  2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社