   弯曲模量 的翻译结果: 查询用时:1.035秒
图标索引 在分类学科中查询
所有学科
有机化工
材料科学
生物医学工程
口腔科学
外科学
生物学
力学
更多类别查询

图标索引 历史查询
 

弯曲模量     
相关语句
  flexural modulus
     2. The tensile strength, flexural strength and flexural modulus of alkali pretreated ramie/LLDPE composite are increased from 51.2 MPa, 23.1 MPa, 1.58 GPa to 102.6 MPa, 30.4 MPa, 1.66 GPa.
     2.经碱液预处理后,苎麻/LLDPE层压复合材料的拉伸强度、弯曲强度和弯曲模量由未处理试样51.2MPa、23.1MPa、1.58GPa提高到102.6MPa、30.4MPa、1.66GPa;
短句来源
     (3) The flexural strength of composites has a value of 30~60MPa, while flexural modulus of 8~12GPa, shear strength of 4~7MPa.
     (3) 复合材料的弯曲强度为30~60MPa,弯曲模量为8~12GPa,剪切强度为4~7MPa。
短句来源
     Specimens with 64mm×10mm×2. 5mm are made for measuring flexural strength and flexural modulus.
     制作64mm×10mm2.5mm的树脂基托试样,用电子万能试验机测量其弯曲强度和弯曲模量
短句来源
     the flexural strength, flexural modulus, total impact energy per unit area and dynamic flexural strength amount to 81.6 MPa, 6.01 GPa, 37.8 kJ/m 2 and 106 MPa from 23.1 MPa, 1.58 GPa, 30.9 kJ/m 2 and 31.1 MPa.
     经 A- 15 1预处理后 ,材料的弯曲强度及弯曲模量由 2 3.1MPa、1.5 8GPa提高到 81.6 MPa、6 .0 1GPa,单位面积总冲击能及动态弯曲强度由 30 .9k J/ m2、31.3MPa提高到 37.8k J/ m2、10 6 MP
短句来源
     The mechanical properties of the NF_WPC prepared according to the optimized formula were as follows: flexural strength 58.7 MPa, flexural modulus 3.0 GPa, tensile strength 39.6 MPa, tensile modulus 4.0 GPa and impact strength 12.7 kJ·m~ -2 respectively.
     采用优化工艺制备的NF-WPC的弯曲强度、弯曲模量、拉伸强度、拉伸模量和冲击强度分别为58·7MPa、3·0GPa、39·6MPa、4·0GPa和12·7kJ·m-2。
短句来源
更多       
  bending modulus
     At the optimal process ing conditions of molding temperature 100 ℃,extruding temperature 100 ℃ and m ould chamber length 10 mm, bending strength of PDLLA/MD and PDLLA/HA/MDI composi tes is 51.3 MPa and 55.4 MPa, respectively and their bending modulus is 1 830.9 MPa and 2068.5 MPa, respectively.
     在模压温度100℃,挤出温度100℃、口模长度10mm的最佳成型工艺条件下,PDLLA/MDI和PDLLA/HA/MDI复合材料的弯曲强度分别为51.3MPa和55.4MPa,弯曲模量分别为1830.9MPa和2068.5MPa。
短句来源
     Results:The shear strength of the HHK-PLA rod is 186 MPa, the bending strength is 230 MPa, and the bending modulus is 12 GPa.
     结果 :HHK -PLA骨科内固定棒的剪切强度为 186MPa ,弯曲强度为 2 30MPa ,弯曲模量为 12GPa。
短句来源
     The fiber volume fraction of the specimen fabricated by bladder-assisted RTM reaches 61.2%, and the bending strength reaches 280.3MPa, and bending modulus 12.79GPa respectively, which are 23% and 34% higher than those of the specimens fabricated by VARTM.
     气囊辅助RTM工艺所制备的试件纤维体积含量达61.2%,弯曲强度达280.3MPa,弯曲模量达12.79GPa,分别比VARTM工艺制备的试件提高了27%、23%、34%。
短句来源
     Results The initial shear strength of HHK-PLA rod was 241 MPa, bending strength 358 MPa, and bending modulus 13 GPa.
     结果(1)HHK-PLA骨科内固定棒具有良好的初始机械力学强度,其剪切强度为241MPa,弯曲强度为358MPa,弯曲模量为13GPa。
短句来源
     RCC has a tensile strength of 46.6 MPa and a bending strength of 95.5 MPa,while the tensile modu- lus and bending modulus is approximately the same,about 10 GPa.
     其拉伸强度为46.6 MPa,弯曲强度高达95.5 MPa,拉伸模量与弯曲模量基本一致,约10 GPa。
短句来源
更多       
  flexure modulus
     After the flexure modulus decreases to less than the 85% of the initial modulus (133 GPa), the changes of the flexure modulus are ruleless.
     其次在弯曲模量下降到原始弯曲模量的 85 % (13 3GPa)后 ,其变化方式没有明显的规律可循 ,有时甚至可能上升 ;
短句来源
     In this paper, the flexure modulus degradation of UD- Cf/SiC composites was studied in three points bending\fatigue test. There were three steps in the change of the flexure modulus as the fatigue progress going on.
     对单向Cf/SiC复合材料进行了三点弯曲疲劳性能测试,研究了Cf/SiC复合材料的疲劳损伤过程中弯曲模量的变化情况。
     With the increase in HA content, the flexural strength and flexure modulus of composites had been greatly increased and the tensile strength of composites had only a little change.
     随着复合材料中HA含量的增加,材料的弯曲强度、弯曲模量有大幅提高,而材料的抗拉强度即韧性降低不大。
短句来源
     In the second step, after the flexure modulus decreased to the 85% of the initial modulus, the change of the flexure modulus was ruleless.
     模量下降到原始弯曲模量156.8GPa的85%(133GPa)后,直至复合材料发生疲劳断裂前,其变化没有明显的规律可循,有时甚至可能上升;
     According to the material structure of 3-D braided composites, a method of stiffness combination is proposed to predict material's flexure modulus. We conducted an analysis of 3 ̄D braided T300/QY9512 composites' flexure modulus with this method.
     根据三维四向编织复合材料的结构特点 ,提出了用刚度合成法来预测复合材料的弯曲模量 ,并对三维编织T30 0 /QY95 12复合材料的弯曲模量进行了预测 .
短句来源
更多       
  bend modulus
     Compared with pure MC nylon , the tesile strength, bend modulus, charpy impact strength increased 21 %, 40.3 %, 69.1 %, the elongation at break decreased 43 %.
     与纯MC尼龙相比,拉伸强度提高21%,弯曲模量提高40.3%,简支梁冲击强度提高69.1%,断裂伸长率降低43%。
短句来源
     It was also revealed that cross-linked polymer was a kind of porous material with the tensile strength,elastic modulus,bend strength and bend modulus of 10.8,86.2,17.7 and 102.3 MPa respectively.
     交联产物为具有一定机械强度和韧性的多孔状材料,其拉伸强度、弹性模量、弯曲强度和弯曲模量的平均值分别为10.8、86.2、17.7和102.3 MPa。
短句来源
     When the mass fraction of KH-550 is 0.2%,the bend strength,bend modulus,tensile strength,tensile stress and impact strength of GFRMCN are increased by 35%,72%,46%,88% and 41%,compared with those of MC nylon. Glass fibers after surface treatment with KH-550 SCA increase the properties of GFRMCN because of a good interface between GF and nylon.
     KH-550质量分数与处理的玻璃纤维质量分数之间符合定量关系式,含量为0.2%时,GFRMCN的弯曲强度提高了35%,弯曲模量提高了72%,拉伸强度提高了46%,弹性模量提高了88%,冲击强度提高了41%。
短句来源
     The results show that FSMF can improve the bend modulus of the resin cast clearly, but reduce the tensile strength.
     结果表明:FSMF显著提高树脂浇铸体的弯曲模量,但降低拉伸强度;
短句来源
     It indicates that the surface modification can enhance the izod impact strength of PP/Mg(OH)_2 composite material by 0.3 kJ/m~2, the bend modulus about 30%, and the retardant degree is enhanced to V0 from V1. The tensile strength of the composite material surface modified with silane FR693 can be increased 1 MPa.
     改性可以使PP/水镁石复合材料的悬臂梁缺口冲击强度提高0.3kJ/m2,弯曲模量提高30%以上,并使材料的阻燃性能提高。
短句来源
更多       

 

查询“弯曲模量”译词为其他词的双语例句

 

查询“弯曲模量”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  flexural modulus
The incorporation of TLCP improves not only the tensile strength and flexural modulus but also the heat distortion temperature (HDT) of the PBT/TLCP composites.
      
In the case of injection molding, the flexural modulus increased with an increase in fiber mass fraction, and the mechanical properties decreased with an increase in cylinder temperature due to the thermal degradation of BF.
      
The influence of the flexible interphase thickness on the flexural modulus and strength are experimentally investigated.
      
Mechanical properties like tensile strength, Young's modulus, flexural strength, flexural modulus and impact strength of the composites containing untreated and alkali-treated fibres have been studied as a function of fibre loading.
      
At 52 weeks the shear strength and flexural modulus of the rods were 41% of the initial value, and the flexural strength was 43% of the initial value.
      
更多          
  bending modulus
The renormalization can be analyzed if the condition g?1 is satisfied (where g~T/κ, T is the temperature, and κ is the bending modulus).
      
For small bending deformations, the ratio between the bending modulus and the area compression coefficient, Kb/KA, is proportional to the square of monolayer thickness h.
      
The NT radii were measured at different values of voltage applied along NT, and the membrane bending modulus was recalculated upon the supposition that the shape of NT deviates from cylindrical only slightly.
      
In addition, bending tests indicated an increase in breaking stress and bending modulus with starch content and -NCO/-OH molar ratio and decreased breaking strain.
      
The effects of the span and the radius of the loading nose on the bending modulus and strength were examined systematically.
      
更多          
  其他


点击这里查询相关文摘
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关弯曲模量的内容
在知识搜索中查有关弯曲模量的内容
在数字搜索中查有关弯曲模量的内容
在概念知识元中查有关弯曲模量的内容
在学术趋势中查有关弯曲模量的内容
 
 