氧化铝黑瓷 alumina black porcelain(4)   alumina black porcelain      Study on Rheological Behavior of Alumina Black Porcelain Slurry      氧化铝黑瓷浆料流变性能的研究 短句来源      Study on Rheological Behavior of Alumina Black Porcelain Slurry      改性氧化铝黑瓷粉体制备高固相含量浆料的研究 短句来源      Effect of Preheating on the Rheological Behavior of Alumina Black Porcelain      预烧处理对氧化铝黑瓷浆料流变性能的影响 短句来源      In this paper,Preheating is used to increase the dimension of alumina black porcelain powder,lower the specific surface energy and improve the rheological behavior of slurry,which is favor to obtain a low viscosity of ceramics suspensions with high solid content.      通过对氧化铝黑瓷粉料进行预烧处理,增大颗粒尺寸,降低比表面能,改善浆料的流变性能,制备出高固相量、低粘度的氧化铝黑瓷稳定浆料。 短句来源   相似匹配句对      Study on Rheological Behavior of Alumina Black Porcelain Slurry      氧化铝黑瓷浆料流变性能的研究 短句来源      Effect of Preheating on the Rheological Behavior of Alumina Black Porcelain      预烧处理对氧化铝黑瓷浆料流变性能的影响 短句来源      TOUGHENING OF ALUMINA CERAMICS      氧化铝陶瓷的增韧 短句来源      present Status of Alumina Hygrometer      氧化铝湿度计的现状 短句来源 查询“氧化铝黑瓷”译词为用户自定义的双语例句     我想查看译文中含有：的双语例句 为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法，我们为您准备了出自英文原文的大量英语例句，供您参考。          Preheating is used to increase the dimension of ceramics powder, lower the specific surface energy and improve the phenomenon of aggregation. The alumina black porcelain slurries containing 55% solid volume were obtained by using the preheating technique. The effects of the amount of dispersant, solid volume fraction and the R ratio on the rheological behaviors of the slurries were studied. The results indicate that rheological behaviors of alumina black porcelain slurries appear shearing thinning and the o...             通过对氧化铝黑瓷粉料进行预烧技术处理,增大颗粒尺寸、降低粉体比表面能、改善其团聚现象,制备出固相体积分数达55%的氧化铝黑瓷稳定料浆,并研究了分散剂用量、体系固相体积分数、R值(塑性剂/粘结剂)对料浆流变性的影响。研究结果表明:浆料的粘度随剪切速率增加而下降,呈剪切稀化的流变学特性,随着固相体积分数的增加,浆料的最佳分散剂用量也相应增加;浆料的粘度随着R值的增加而急剧减小,流变性能得到明显改善。 文摘来源          In this paper,Preheating is used to increase the dimension of alumina black porcelain powder,lower the specific surface energy and improve the rheological behavior of slurry,which is favor to obtain a low viscosity of ceramics suspensions with high solid content.The results indicate that the optimum preheating temperature is 900℃ for the dimension and specific surface energy of ceramics powder,and it is clear that the rheological behaviors of alumina black porcelain slurries are improved obviously and solid...             通过对氧化铝黑瓷粉料进行预烧处理,增大颗粒尺寸,降低比表面能,改善浆料的流变性能,制备出高固相量、低粘度的氧化铝黑瓷稳定浆料。研究结果表明:随着预烧温度的升高,粉料比表面积减小,预烧使粉料活性略有下降,综合考虑900℃是较合适的预烧温度。预烧处理明显改善了浆料的流变性能,由900℃预烧处理的粉料可制备出55vol%高固相体积分数的浆料。 文摘来源          Preheating is used to increase the dimension of ceramics powder,lower the specific surface energy and improve the phenomenon of aggregation.The alumina black porcelain slurries containing 55% solid volume were obtained by using the preheating technique.The effects of the amount of dispersant,solid volume fraction and the R ratio on the rheological behaviors of the slurries were studied.The results indicate that rheological behavior of alumina black porcelain slurries appear shearing thinning and the optimum...             通过对氧化铝黑瓷粉料进行预烧技术处理,增大颗粒尺寸、降低粉体比表面能、改善其团聚现象,制备出固相体积分数达55%的氧化铝黑瓷稳定料浆,并研究了分散剂用量、体系固相体积分数、R值(塑性剂/粘结剂)对料浆流变性的影响。结果表明:浆料的粘度随剪切速率增加而下降,呈剪切稀化的流变学特性,随着固相体积分数的增加,浆料的最佳分散剂用量也相应增加;浆料的粘度随着R值的增加而急剧降低,流变性能得到明显改善。 文摘来源   << 更多相关文摘         相关查询: 氧化铝 黑瓷 活性氧化铝 氮氧化铝 氧化铝瓷 重结晶氧化铝 多孔氧化铝 氧化铝市场 氧化铝封装 氧化铝纤维 氧化铝模板 氧化铝含量  对查询结果不满意

CNKI小工具 在Springer中查有关的英文论文 在知识搜索中查有关氧化铝黑瓷的内容 在数字搜索中查有关氧化铝黑瓷的内容 在概念知识元中查有关氧化铝黑瓷的内容 在学术趋势中查有关氧化铝黑瓷 的内容

CNKI主页 |  设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务

2008 CNKI－中国知网

京ICP证040431号 互联网出版许可证 新出网证(京)字008号 北京市公安局海淀分局 备案号：110 1081725  2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社