     Compared with the direct-bonded magnesia-chromite brick,the magnesia-hercynite brick has the superior thermal shock resistance and the similar adhesive strength(coatability).
     与直接结合镁铬砖相比,镁铁铝尖 晶石砖在热震稳定性方面更优于直接结合镁铬砖,而 在粘挂窑皮性能方面与其相近。
短句来源
  相似匹配句对
     Application of alumina-magnesia spinel brick in ladle
     尖晶石在盛钢桶上的应用
短句来源
     Effect of spinel on slag resistance of the aluminium-spinel-carbon bricks
     尖晶石尖晶石抗渣性的影响
短句来源
     Corundum-spinel brick used in ladle
     钢包用刚玉-尖晶石
短句来源
     DISCOVERY OF Al-Si SPINEL IN NATURE
     硅尖晶石在自然界的发现
短句来源
     ALUMINA-SPINEL CASTABLES FOR LADLE LINING
     钢包用尖晶石浇注料
短句来源
查询“铝尖晶石砖”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


Fused magnesia-alumina spinel and medium magnesite cliker were used as starting material to prepare MA-spinel brick,which has good thermal shock resistance of 38 cycles under the condition of water-1100℃.The application of the brick in large dry-method cement kiln has shown good results which can be compared to the similar import brick from German.

以电熔镁铝尖晶石和中档镁砂为原料,采用适当的工艺研制了镁铝尖晶石砖。制品性能优良,尤其是热震稳定性(1100℃,水冷)高达38次。制品在大型干法水泥回转窑冷却带使用,效果达到了西德雷法公司的同类产品水平。

Refractories used in cement kiln consist of clay bricks, alumina bricks, phosphate-bonded alumina lining bricks, magnesium bricks, magnesium aluminate spinel bricks, ordinary chrome-magnesite bricks, directly bonded chrome-magnesite bricks etc. They can be matched to different location in kiln system according to their different properties.

水泥窑用耐火材料有粘土砖、高铝砖、磷酸盐结合高铝质窑衬砖、镁砖、镁铝尖晶石砖、普通镁铬 砖、直接结合镁铬砖等等,根据它们不同性能分别匹配于窑系统的不同部位。

The magnesia-hercynite brick was prepared using magnesite with particle size 3.5~1 mm,<1 mm and <0.088 mm and hercynite <2 mm as starting materials to meet the need for chromite-free brick of the burning zone of cement rotary kiln.Effects of firing temperature 1500 ℃,1550 ℃,1600 ℃ and 1650 ℃ and hercynite addition 5%,7%,9% and 11% on properties of the brick were studied.The results show that the magnesia-hercynite specimen fired at 1600 ℃ was densified,and the specimen with 7% hercynite has the highest cold...

The magnesia-hercynite brick was prepared using magnesite with particle size 3.5~1 mm,<1 mm and <0.088 mm and hercynite <2 mm as starting materials to meet the need for chromite-free brick of the burning zone of cement rotary kiln.Effects of firing temperature 1500 ℃,1550 ℃,1600 ℃ and 1650 ℃ and hercynite addition 5%,7%,9% and 11% on properties of the brick were studied.The results show that the magnesia-hercynite specimen fired at 1600 ℃ was densified,and the specimen with 7% hercynite has the highest cold crushing strength and adhesive strength(showing its coatability).Compared with the direct-bonded magnesia-chromite brick,the magnesia-hercynite brick has the superior thermal shock resistance and the similar adhesive strength(coatability).

为了满足水泥窑烧成带用砖无铬化的要求, 以粒度3.5~1mm、<1mm、<0.088mm的高铁镁 砂和粒度<2mm的铁铝尖晶石为原料,分别讨论了 1500℃、1550℃、1600℃、1650℃的烧成温度和 5%、7%、9%、11%的铁铝尖晶石加入量对镁铁铝尖 晶石砖性能的影响。结果表明:当烧成温度为1600 ℃时,试样已烧结;当铁铝尖晶石加入量为7%时,试 样的耐压强度与粘结强度最高(用粘结强度表征材 料的挂窑皮性)。与直接结合镁铬砖相比,镁铁铝尖 晶石砖在热震稳定性方面更优于直接结合镁铬砖,而 在粘挂窑皮性能方面与其相近。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关铝尖晶石砖的内容
在知识搜索中查有关铝尖晶石砖的内容
在数字搜索中查有关铝尖晶石砖的内容
在概念知识元中查有关铝尖晶石砖的内容
在学术趋势中查有关铝尖晶石砖的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社