助手标题  
全文文献 工具书 数字 学术定义 翻译助手 学术趋势 更多
查询帮助
意见反馈
   冷卷 的翻译结果: 查询用时:0.012秒
图标索引 在分类学科中查询
所有学科
机械工业
更多类别查询

图标索引 历史查询
 

冷卷
相关语句
  cold-coiling
     Unloading-resilience of Cold-coiling Sprial Spring
     冷卷螺旋弹簧的卸载回弹
短句来源
  cold winding
     Study on the Heat Treating Technology and Microstructure of 60Si_2 MnA Spring Steel for the Cold Winding Spring
     60Si_2MnA钢冷卷弹簧热处理工艺及显微组织的研究
短句来源
     Practical Analyzation on Working on the Drum of Flat Rotary Curing Press with a Method of Complete Cold Winding Weld
     用整体冷卷焊接法加工平带鼓式硫化机鼓体的实用分析
短句来源
     This paper deals with the heat treating technology of the φ20mm 60Si2MnA spring steel for the cold winding spring. The experimental results show that the fine lath martensite structure can be obtained when the quenching temperature is properly raised. After tempered at 45—460℃, the satisfactory combined mechanical property can be obtained.
     采用直径20mm的60Si2MnA冷卷弹簧热处理工艺,并适当提高加热温度,淬火后得到细板马氏体,经45O—46O℃回火,获得满意的综合机械性能。
短句来源
     Analyzed the relationship of parameters of complete cold winding drum、 curing pressure、 precision of finished product、 steel plate size and the winding-up equipment.
     分析了整体冷卷鼓体参数、硫化压力、制品精度、钢板规格及卷制设备能力间的关系。
短句来源
  “冷卷”译为未确定词的双语例句
     The scale density calculated of as hot coiled strip and of cooled coil is 5.49 g/cm~3 and 5.19 g/cm~3 respectively.
     计算得出单张板氧化皮密度为5.49g/cm~3,冷卷的氧化皮密度为5.19g/cm~3;
短句来源
     The scale on button side is thicker than that one on upper side of strip; The relation of the as hot coiled strip's scale thickness X(μm) with strip thickness h(mm) is X = 3.957+2.096A , cooled coil is X = 3.684+2.209h and X= 8.152 + 3.132h is for THCR;
     冷卷氧化皮厚度X(μm)—板厚h(mm)间的关系X=3.957+2.096h,单张板的关系为X=3.684+2.209h,传统热连轧条件下为X=8.152+3.132h。
短句来源
     Heuristic Algorithm of Scheduling Model for Cold Coils Annealing
     冷卷热处理生产调度模型的启发式算法
短句来源
     Discuss about Wrapping Technique Improvement of the Spring
     关于冷卷弹簧试卷工艺改进的探讨
短句来源
     The scale composition is strongly influenced by cooling condition, the scale of cooled coil consist mainly from Fe3O4 and differ from lab result obviously.
     发现:轧后冷却过程对氧化皮的组成有显著影响,冷卷的氧化皮基本上由Fe3O4组成,显著区别于以往实验室研究的结果;
更多       
  相似匹配句对
     Unloading-resilience of Cold-coiling Sprial Spring
     螺旋弹簧的卸载回弹
短句来源
     THE MEASUREMENT OF THE HEIGHT OF“CONVEX CLOSURE”ON COLD COIL
     轧钢“鼓包”高度的测量方法
短句来源
     On cold fusion
     核聚变
短句来源
     Cold Mountain
     《山》
短句来源
     National Matriculation English Test(NMET 2000)
     英语(全国)
短句来源
查询“冷卷”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


This paper deals with the heat treating technology of the φ20mm 60Si2MnA spring steel for the cold winding spring. The experimental results show that the fine lath martensite structure can be obtained when the quenching temperature is properly raised. After tempered at 45—460℃, the satisfactory combined mechanical property can be obtained.

采用直径20mm的60Si2MnA冷卷弹簧热处理工艺,并适当提高加热温度,淬火后得到细板马氏体,经45O—46O℃回火,获得满意的综合机械性能。

This paper analyses the curvature between initial and cold-formed states of S-Mainspring by the theory of plasticity then the equation can be derived for the bending moment in any location of the mainspring. A theoretical basis is provided for calculation of the shape and moment of the mainspring.

应用塑性力学理论,分析S型发条无应力状态与冷卷成型状态的曲率,导出计算发条截面弯矩的计算式,为计算S型发条的形态与力矩提供了理论依据。

The residual stress on the surface of the wrought tin brass HSn70-1 was measured by means of the resistance strain gauge. The influence of drawing deformation parameters on the tube's residual stress and other properties are analyzed in the paper. The results show that increase of the wall thickness reduction resultes in a remarkable decrease in the drawing residual stress on the tube's surface. Increasing the reduction ratio of wall thickness t0/t1beyond 1.2, decreases the residual stress of the drawn...

The residual stress on the surface of the wrought tin brass HSn70-1 was measured by means of the resistance strain gauge. The influence of drawing deformation parameters on the tube's residual stress and other properties are analyzed in the paper. The results show that increase of the wall thickness reduction resultes in a remarkable decrease in the drawing residual stress on the tube's surface. Increasing the reduction ratio of wall thickness t0/t1beyond 1.2, decreases the residual stress of the drawn tube and refines the grain size after final annealing. The surface residual stress of tubes manufactured by different methods also follows the same law. A tube made by a two-high cold mill has been subjected to a great reduction of wall thickness resulting in large compressive surface stresses. On the other hand, a tube coil made by cold drawing has no wall thickness reduction, and have no large tensile stress on its surface. After evaluating the drawn tube′s annealing technological parameters and its grain size, through-speed and annealing temperature of the drawn tube in the roller-hearth continuous annealing furnace have been optimized. Fine uniform recrystallized structures in the wrought tube has been obtained along with a release of much of the residual stress.

用电阻应变片法测试了变形锡黄铜HSn70-1管材表面的残余应力,分析了拉拔管材变形参数对管材表面残余应力及其他性能指标的影响规律。结果表明,增大管材的减壁变形,可以显著地减小管材表面的拉伸残余应力,当减壁比t0/t1大于1.2时,拉拔管材的残余应力较小,经成品退火后管材晶粒组织细小。采用不同变形方法生产的管材,其表面残余应力也遵循这一规律。2辊冷轧管材有很大的减壁变形,其表面产生了很大的压应力,而冷卷管材无减壁变形,则表面产生了很大的拉应力。对拉拔变形管材退火工艺参数进行了试验,用管材晶粒度指标进行评价,优化了辊底式连续退火炉管材通过速度和退火温度,保证管材获得均匀细小的再结晶组织,较好地消除了变形管材的残余应力。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关冷卷的内容
在知识搜索中查有关冷卷的内容
在数字搜索中查有关冷卷的内容
在概念知识元中查有关冷卷的内容
在学术趋势中查有关冷卷的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社