   外热防护 在 航空航天科学与工程 分类中 的翻译结果: 查询用时:0.077秒
图标索引 在分类学科中查询
所有学科
航空航天科学与工程
更多类别查询

图标索引 历史查询
 

外热防护
相关语句
  external thermal protection
    Study on a external thermal protection coating material for spacecraft
    一种航天器用外热防护涂层材料研究
短句来源
    A kind of external thermal protection coating material which takes epoxy-modified organic silicone resin and polyamide curing agent as matrix,and thermal-insulating and heat-resisting fillers as additives was developed.
    研制了一种由环氧改性有机硅树脂、聚酰胺类固化剂为基体,以隔热及耐热填料为添加剂的室温固化耐高温外热防护涂料体系;
短句来源
  external thermal protection
    Study on a external thermal protection coating material for spacecraft
    一种航天器用外热防护涂层材料研究
短句来源
    A kind of external thermal protection coating material which takes epoxy-modified organic silicone resin and polyamide curing agent as matrix,and thermal-insulating and heat-resisting fillers as additives was developed.
    研制了一种由环氧改性有机硅树脂、聚酰胺类固化剂为基体,以隔热及耐热填料为添加剂的室温固化耐高温外热防护涂料体系;
短句来源
  “外热防护”译为未确定词的双语例句
    This coating can be used as external heat-insulating coating for carbon fiber/epoxy composite case.
    涂料采用丙酮和二甲苯作为混合溶剂,可用于碳纤维/环氧复合材料壳体表面的外热防护
短句来源
查询“外热防护”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


A kind of external thermal protection coating material which takes epoxy-modified organic silicone resin and polyamide curing agent as matrix,and thermal-insulating and heat-resisting fillers as additives was developed.The material with high temperature resistant property was cured at room temperature.Tensile strength of the coating material is up to 3.15MPa,elongation-to-break 26%,thermal conductivity coefficient 0.271W/(m·K),and specific heat capacity 2.689J/(g·K).At the same time,the coating material possesses...

A kind of external thermal protection coating material which takes epoxy-modified organic silicone resin and polyamide curing agent as matrix,and thermal-insulating and heat-resisting fillers as additives was developed.The material with high temperature resistant property was cured at room temperature.Tensile strength of the coating material is up to 3.15MPa,elongation-to-break 26%,thermal conductivity coefficient 0.271W/(m·K),and specific heat capacity 2.689J/(g·K).At the same time,the coating material possesses better heat-insulating property,heat-resisting property and excellent adhesion.The coating material can be used for the external thermal protection of T700/4319 composite material case surface,and it can be used at the temperature of 350℃ for a short period.

研制了一种由环氧改性有机硅树脂、聚酰胺类固化剂为基体,以隔热及耐热填料为添加剂的室温固化耐高温外热防护涂料体系;该外热防护涂层材料的拉伸强度3.15MPa,断裂伸长率26%;热导率0.271W/(m.K),比热容2.689 J/(g.K),而且具有优良的隔热性能、耐热性能以及良好的附着力。该涂层材料可用于T700/4319复合材料壳体表面的外防护,并可在350℃温度条件下短期使用。

The external coating which is based on the epoxy resin modified silicone resin and can be cured at room temperature is developed.The results show that the thermal conductivity and specific heat capacity of the coating is 0.266 W/(m·K) and 1.993 kJ/kg·K respectively.Tensile strength of the coating is 3.15 MPa and tensile elongation is 30%.At the same time,the coating has excellent ablative properties and good adhesive properties with carbon fiber/epoxy resin composite.The coating can stand high temperature up...

The external coating which is based on the epoxy resin modified silicone resin and can be cured at room temperature is developed.The results show that the thermal conductivity and specific heat capacity of the coating is 0.266 W/(m·K) and 1.993 kJ/kg·K respectively.Tensile strength of the coating is 3.15 MPa and tensile elongation is 30%.At the same time,the coating has excellent ablative properties and good adhesive properties with carbon fiber/epoxy resin composite.The coating can stand high temperature up to 450℃ for a short period,and the coating owns well consistent property to carbon fiber/epoxy resin composite as well,the solvent of the coating is a mixture of acetone and xylene.This coating can be used as external heat-insulating coating for carbon fiber/epoxy composite case.

研制了一种室温固化环氧改性有机硅树脂涂料。研究结果显示,涂料热导率为0.266W/(m.K),比热容为1.993kJ/kg.K;拉伸强度为3.15MPa;断裂伸长率为30%;并具有较好的耐烧蚀性能以及良好的附着力;该涂层短时可耐450℃的高温,并且与碳纤维/环氧复合材料之间具有良好的界面相容性;涂料采用丙酮和二甲苯作为混合溶剂,可用于碳纤维/环氧复合材料壳体表面的外热防护

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关外热防护的内容
在知识搜索中查有关外热防护的内容
在数字搜索中查有关外热防护的内容
在概念知识元中查有关外热防护的内容
在学术趋势中查有关外热防护的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社