  slag composition
     The components involving slag composition are divided into 2 categories,namely ①quadribasic series SiO_2-CaO-MgO-Al_2O_3,base salinity variation being 0. 9~1. 3;
     研究的炉渣成份主要分成两大类,分别是①四元系列的SiO_2-CaO-MgO-Al_2O_3,盐基度变化为0.9~1.3;
短句来源
  “炉渣成份”译为未确定词的双语例句
     Thus, if the Cr_2O_3 concentration in the slag is maintained below 4%, it should not be difficult to refine chromium-containing hot metal.
     在吹炼含铬半钢情况下,若用红砖作助熔剂,同时炉渣成份控制在下列范围内,CaO/SiO_2=3~5,Cr_2O_3<7%, ∑FeO~20%, Al_2O_3≈3%,,成渣温度火致在1280~1360℃. 工业试验证明,吹炼操作顺利,渣化得快,化得透.
短句来源
     This paper introduces the effect of reaction at static state and che influence of slags composition,temperature of slags and hot metal on silicon transmission in the blast furnace.
     本文介绍渣—铁之间静止状态下的反应对高炉内硅迁移曲作用及炉渣成份和渣铁湿度对硅迁移的影响。
短句来源
     This paper aims to give an introduction to relationship between slag viscosity and variables of slag components and temperature.
     本文主要希望介绍熔融还原炼铁法炉渣黏度与炉渣成份及温度等变数之关系。
短句来源
  相似匹配句对
     Determination of Major Elements in Converter Slag by XRF
     X射线荧光光谱法测定转炉渣主要成份
短句来源
     Treating Methods for BF Slag
     高炉渣处理方法
短句来源
     Reclamation and Utilization of the Slag from Power Plant
     燃煤炉渣的回收利用
短句来源
     Nutritional Constituents of Bamboo Shoots
     竹笋的营养成份
短句来源
     ②fat;
     ②脂肪成份 ;
短句来源
查询“炉渣成份”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  slag composition
The value ofU is found to have a slight dependence on slag temperature, slag composition, and slag-skin thickness.
      
It is inferred from the results that the slag composition chosen could probably be used to electroslag weld thick sections of titanium.
      
The model was applied to commercial slag-matte systems, and the reduction of sulfur solubility by changing the slag composition was concluded to be the key in reducing copper losses to slag, especially for mattes containing less than 50 pct Cu.
      
The effect of slag composition has also been studied.
      
The absolute values of the heat flux and their variation within the region adjacent to the liquid slag were shown to be dependent upon the slag composition and the remelting conditions.
      
更多          


The melting temperatures of certain slags containing chromic oxide have been determined. The presence of 2%Cr_2O_3 decreases the slag formation temperature by 30~80℃, while more than 4% Cr_2O_3 in the slag raises the slag formation temperature to about 1450℃. Thus, if the Cr_2O_3 concentration in the slag is maintained below 4%, it should not be difficult to refine chromium-containing hot metal.

测定了含Cr_2O_3炉渣的成渣温度.渣中含有少量(≈2%)Cr_2O_3,可使成渣温度下降30~80℃,Cr_2O_3含量超过4%,成渣温度又上升到1450℃±.因此在吹炼含铬铁水时,若渣中Cr_2O_3含量控制在4%以下时,吹炼操作不会有困难.在吹炼含铬半钢情况下,若用红砖作助熔剂,同时炉渣成份控制在下列范围内,CaO/SiO_2=3~5,Cr_2O_3<7%, ∑FeO~20%, Al_2O_3≈3%,,成渣温度火致在1280~1360℃.工业试验证明,吹炼操作顺利,渣化得快,化得透.对红砖的助熔作用也作了初步观察.

The main components in slag are calcium oxide, silicon dioxide,ferrous iron, manganese oxide, aluminium sesquioxide and a micro-amount of magnesium oxide, phosphorus pentoxide, and so on. Components of the slag formed vary with refractory materials used in the cupola and casting techniques.

炉渣中主要成份是氧化钙、二氧化硅、亚铁、氧化锰、三氧化二铝和少量氧化镁、五氧化二磷等。由于冲天炉所用耐火材料及铸造工艺的不同,所形成的炉渣成份各有差异。 本文设计实验了冲天炉炉渣高速分析法。经过两年多时间,近百次测试所得数据证实,本方法是成功的,获得了满意的分析结果并用于生产实际。此方法的特点是:分析程序简便,容易掌握、高速(15~20分钟)。

This paper introduces the effect of reaction at static state and che influence of slags composition,temperature of slags and hot metal on silicon transmission in the blast furnace.

本文介绍渣—铁之间静止状态下的反应对高炉内硅迁移曲作用及炉渣成份和渣铁湿度对硅迁移的影响。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关炉渣成份的内容
在知识搜索中查有关炉渣成份的内容
在数字搜索中查有关炉渣成份的内容
在概念知识元中查有关炉渣成份的内容
在学术趋势中查有关炉渣成份的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社