  oxygen absorbing film
     An oxygen absorbing resin was obtained by dispersing iron based deoxidizing agent into PE-LD matrix containing a small fraction of EVOH. The resin was then blended with additional PE-LD in a single screw extruder to obtain an oxygen absorbing film via blow molding.
     采用铁系脱氧剂、乙烯-乙烯醇共聚物(EVOH)、相容剂和PE-LD,通过双螺杆挤出机制备吸氧母料,将其与适量PE-LD混合经单螺杆挤出机吹塑成吸氧薄膜
短句来源
  “吸氧薄膜”译为未确定词的双语例句
     The influences of the film composition, environmental temperature and humidity on the oxygen absorbing performance were examined.
     考察了吸氧薄膜配方、温度和湿度对吸氧性能的影响。
短句来源
  相似匹配句对
     Silan-based Thin Films
     硅烷薄膜
短句来源
     Physcis of the Thin Film
     《薄膜物理学》
短句来源
     The influences of the film composition, environmental temperature and humidity on the oxygen absorbing performance were examined.
     考察了吸氧薄膜配方、温度和湿度对吸氧性能的影响。
短句来源
     the absorption and desogtion of oxygen in annealing were found to occur at 330 ℃.
     对薄膜热处理时,薄膜吸氧或放氧发生在330℃以上。
短句来源
     All rabbits were given no oxygen inhalation.
     均不吸氧
短句来源
查询“吸氧薄膜”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


An oxygen absorbing resin was obtained by dispersing iron based deoxidizing agent into PE-LD matrix containing a small fraction of EVOH. The resin was then blended with additional PE-LD in a single screw extruder to obtain an oxygen absorbing film via blow molding. The influences of the film composition, environmental temperature and humidity on the oxygen absorbing performance were examined. It was found that the capacity of oxygen absorbing increased with the increasing content of iron based deoxidizing agent...

An oxygen absorbing resin was obtained by dispersing iron based deoxidizing agent into PE-LD matrix containing a small fraction of EVOH. The resin was then blended with additional PE-LD in a single screw extruder to obtain an oxygen absorbing film via blow molding. The influences of the film composition, environmental temperature and humidity on the oxygen absorbing performance were examined. It was found that the capacity of oxygen absorbing increased with the increasing content of iron based deoxidizing agent and EVOH in the film, environmental temperature and humidity, however, decreased with increasing film thickness.

采用铁系脱氧剂、乙烯-乙烯醇共聚物(EVOH)、相容剂和PE-LD,通过双螺杆挤出机制备吸氧母料,将其与适量PE-LD混合经单螺杆挤出机吹塑成吸氧薄膜。考察了吸氧薄膜配方、温度和湿度对吸氧性能的影响。结果表明,随着铁系脱氧剂和EVOH含量的增加、环境温度的提高以及环境湿度的变大,薄膜吸氧量会随之增加;随着薄膜厚度的增加,薄膜吸氧量减少。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关吸氧薄膜的内容
在知识搜索中查有关吸氧薄膜的内容
在数字搜索中查有关吸氧薄膜的内容
在概念知识元中查有关吸氧薄膜的内容
在学术趋势中查有关吸氧薄膜的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社