单晶组织 single crystal organization(0) single crystal structures(1)   single crystal structures      The device is a complex synthetic body of energies, in which vaccum system, water - cooling system and autocontrol system of vaccum and temperature at a series of points are installed. The device can ue used for manufacturing blades with colum or single crystal structures at the velocity of solidification 10-~20 mm/min by comparison with the general directional solidification velosity of 2--4 mm/min.      该装置为一复杂机能的综合体,设有真空、水冷及在一系列点上自动控制真空和温度的系统,可用于制造具有柱状单晶组织的叶片,其结晶速度为10～20mm/min,而一般定向结晶工艺的结晶速度为2～4mm/min。 短句来源   “单晶组织”译为未确定词的双语例句      Response of Microstructure of DD32 Single Crystal to Electron Beam Floating Zone Melting Directional Solidification      DD32单晶组织对电子束浮区熔炼技术定向凝固的响应 短句来源      Tensile tests show that the maximum tensile strength is 910 MPa,elongation 18.76%,which are equivalent to that of single crystal structure,much better than that of polycrystalline structure.      拉伸试验显示其抗拉强度最高达910MPa,伸长率18.76%,与单晶组织相近而远优于多晶组织; 短句来源      This technology can make the microstructure of material to be aligned exactly along with the preferential orientation and then can obtain unidirectional domains or single crystal, so the research, which is preparing high temperature superconductor with stronger anisotropism by the unidirectional solidification method, is being paid more attention.      而定向凝固技术可使材料显微结构按择优生长方向规整排列,获得定向或单晶组织,故用此技术制备具有强各向异性的高温超导体的研究受到了高度重视。 短句来源      Whether the single crystal can be obtained or not depends on the profile of the solid liquid interface which is influenced by the casting s peed.      工艺 参数对铸锭单晶组织演化过程的影响是通过影响液固界面的形状而起作用的。 短句来源      An Al-1%Si bar with 8 mm in diameter and single crystal was made with self-made vacuum vertical continuous unidirectional casting equipment. The microstructure evolution and stability during continuous unidirectional solidification were studied.      在自制的真空熔炼、氩气保护下拉式连续定向凝固设备上成功制取了具有单晶组织的φ8mm Al-1％Si合金棒材,并对其组织演变过程及稳定性进行了研究. 短句来源 更多          相似匹配句对      Organization      组织 短句来源      Effect of Sample Size on Solidified SC Structure      单晶凝固组织的样品尺寸效应 短句来源      The structure and property of deformed single crystal Al wire      变形单晶铝线材的组织和性能研究 短句来源      Organising Committee      组织委员会 短句来源      MgO SINGLE CRYSTAL      MgO单晶 短句来源 查询“单晶组织”译词为用户自定义的双语例句     我想查看译文中含有：的双语例句 为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法，我们为您准备了出自英文原文的大量英语例句，供您参考。   single crystal structures In order to confirm the information obtained by those techniques, the X-ray single crystal structures of methyl 12-acetyldehydroabietate and methyl 12-(4-methoxycinnamoyl)-dehydroabietate were determined. 例句来源       The mechanism of the solid-solid transition can be explained by analyzing the molecular packing information gained from the single crystal structures. 例句来源       Synthesis of s-fac/mer bis(N2-methyldiethylenetriamine, L) nickel(II): X-ray single crystal structures of s-fac[NiL2](NO3)2 and 例句来源       [NiL2](NO3)2 (1) and [NiL2](CF3CO2)2 (2) (L = N2-methyldiethylenetriamine] have been synthesized and their X-ray single crystal structures have been determined. 例句来源       Synthesis, characterization and single crystal structures of one-dimensional coordination polymers formed with [Ni(L)]·2ClO4 and 例句来源       更多                    In this paper the directional solidification process of blades in gas turbine engine of former Sovit Union and the special device used for the process are described. The device is a complex synthetic body of energies, in which vaccum system, water - cooling system and autocontrol system of vaccum and temperature at a series of points are installed. The device can ue used for manufacturing blades with colum or single crystal structures at the velocity of solidification 10-~20 mm/min by comparison with the ge...             本文介绍前苏联燃气涡轮发动机叶片高速定向结晶工艺和为此工艺专门创制的УВНК-8П装置。该装置为一复杂机能的综合体,设有真空、水冷及在一系列点上自动控制真空和温度的系统,可用于制造具有柱状单晶组织的叶片,其结晶速度为10～20mm/min,而一般定向结晶工艺的结晶速度为2～4mm/min。 文摘来源          The relationship between Ni_3Al single crystal structures with Boron contents of 0, 0.52, 1.37, 2.22 and 3.00 at % and their mechanical properties at room and high temperatre is studied in this paper. It shows that as the Boron content grows, the tensile strength and yield strength of Ni_3Al single crystal at room temperature and 800℃ increase continuously. The maximums are obtained at contents of 1.37 and 0.52at % B respectively. If the Boron content continue to grow, boride eutectic will separate out from...             本文研究了硼含量为0、0.52、1.37、2.22和3.00at％的Ni_3Al单晶的组织以及在室温和高温的力学性能。结果表明,随着硼含量增加,室温和800℃的抗张强度和屈服强度不断提高,分别在1.37和0.52at％B时达到最高值,进一步提高硼含量,由于组织中析出硼化物共晶而使性能恶化。850℃,100MPa条件下的持久时间和持久延伸率均随硼含量的提高而不断地明显降低,但与同样成分的多晶Ni_3Al比较,它们都提高1个或2个数量级。 文摘来源          The microstructure and high temperature stress rupture properties of a nickel-base single crystal superalloy NASAIR100 cast in both high and low thermal gradients have ben investigated comparatively. It was found that the high thermal gradient casting enhanced reductions in dendrite arm spacing and in the amount of casting porosity. The high thermal gradient cast single crystals possessed finer,more regular γ′Precipitates and less γ/γ′cutectic. With the same withdrawal rate, the high thermal gradient castin...             对比了高温度和低温度梯度下ＮＡＳＡＩＲ１００单晶的组织和高温持久性能，发现高温度梯度降低单晶中显微疏松含量，减小树枝晶间里和显微偏析程度，使单晶具有较少的γ／γ′共晶和较细的，形状较规则的γ′沉淀．在相同的抽拉速率下，高温度梯度提高铸态ＮＡＳＡＩＲ１００单晶的高温持久寿命可达１１倍多，固溶处理进一步改进单晶的组织和高温持久性能． 文摘来源   << 更多相关文摘         相关查询: 组织 组织( 单晶 组织基因 出版组织 临时组织 组织剩余 联合国资本开发基金组织 触变组织 组织素材 冷却组织 组织协作  对查询结果不满意

CNKI小工具 在Springer中查有关的英文论文 在知识搜索中查有关单晶组织的内容 在数字搜索中查有关单晶组织的内容 在概念知识元中查有关单晶组织的内容 在学术趋势中查有关单晶组织 的内容

CNKI主页 |  设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务

2008 CNKI－中国知网

京ICP证040431号 互联网出版许可证 新出网证(京)字008号 北京市公安局海淀分局 备案号：110 1081725  2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社