   复合夹杂 的翻译结果: 查询用时:0.495秒
图标索引 在分类学科中查询
所有学科
冶金工业
更多类别查询

图标索引 历史查询
 

复合夹杂
相关语句
  complex inclusions
     Most of the inclusions are silicate of silicon aluminum, little are large-scale complex inclusions that is mainly Al2O3 in the center or some surrounded by a layer of silicate of silicon aluminum.
     大型复合夹杂物中心或某一区域为Al2O3相,外裹硅铝酸盐相,个别复合夹杂中含硫化物。
短句来源
     The grade and distribution of inclusion in (800~1200)mm×180 mm concasting slab produced by extra-low head concaster have been analyzed. The inclusions in slab mainly consist of complex inclusions and MnS, and the amount of inclusion obviously increases at inside of slab due to the small curve-shaped radius of extra-low head concaster.
     分析了 (80 0~ 1 2 0 0 )mm× 1 80mm超低头连铸板坯夹杂物的类型和分布 ,板坯中的夹杂物主要由复合夹杂和MnS组成 ,因超低头连铸机弧形半径较小 ,板坯内侧夹杂数量明显增多
短句来源
     The results show that: 1) Slab inclusions include deoxidation product, sulphide, complex inclusions composed of sulphide and deoxidation product; 2) Complex inclusions composed of some adventitious inclusions and deoxidation product, furthermore main inclusions are spherical inclusions; 3)Inclusions of diameter greater than 280μm can be got rid of in the mould, but inclusions of diameter between 50~280μm can not be got rid of effectively.
     研究表明,板坯中非金属夹杂物包括脱氧产物、硫化物、硫化物与脱氧产物形成的复合夹杂以及少量的由外来夹杂物和脱氧产物形成的复合夹杂物,以球状硅酸盐夹杂为主,在结晶器内大于280μm的夹杂物能够去除,而直径在50~280μm之间的夹杂物没能有效去除。
短句来源
  “复合夹杂”译为未确定词的双语例句
     The experimental findings showed that feeding SiCaBa wire had better effect on inclusion modification and decreasing total oxygen content than feeding SiCa wire Moreover, inclusion components changed from Al2O3 into mCaO· nAl2O3 or compound inclusions consisting of CaO, Al2O3 and SiO2 and morphology of inclusions changed into globular shape, accordingly, the capabilities of steel would be improved.
     结果表明,喂SiCaBa线效果优于喂SiCa包芯线,钢中的全氧含量和夹杂物面积均有所降低,而且脱氧产物由Al2O3转变为mCaO·nAl2O3或者CaO-Al2O3-SiO2复合夹杂,从形貌上看近乎完全球化,对于提高钢材质量具有很大意义。
     (4)The main inclusion of the X80 steel was the series of CaO-MgO-Al_2O.
     (4)X80钢中的夹杂物以CaO-MgO-Al_2O复合夹杂为主;
短句来源
     Using the thermodynamic data and the practical data of Tianjin Steel Pipe Co, the relation of calcium \| aluminium in steel :[%Al]\+2/[%Ca]\+3 < 1.98x10\+5, that was available to form liquid calcium aluminate inclusion to float up, was obtained by thermodynamic calculation as the molten steel was fed CaSi core wire.
     利用热力学数据和天津钢管公司实际生产数据,经热力学计算,得到钢液喂Ca 生成易上浮排除的液态钙、铝复合夹杂,钢中CaAl 比必须满足[ % Al]2/[ % Ca]3 < 1.98×105 。
短句来源
     The following results are observed:the total oxygen content of slab is 0.00147 % and 0.00182 %, the number of the micro inclusions is 2.78 piece/mm 2, and the number of the macro inclusions is 1.13 mg/(10 kg) steel, which means the steel cleanliness is quite good. In addition, the inclusions have almost totally been modified into calcium aluminate and complex calcium aluminate with CaS.
     研究表明 ,铸坯中 T[O]平均值为 0 .0 0 14 7%和 0 .0 0 182 % ,显微夹杂物为 2 .78个 / m m2 ,大型夹杂物数量为 1.13mg/ (10 kg) ,各项洁净度指标均达到了很高水平 ,同时夹杂物已基本变性为钙铝酸盐及钙铝酸盐与硫化钙组成的复合夹杂
短句来源
     The non-metallic inclusions in the normal slabs at the casting middle period is mainly small size Al2O3 blocks (≤30 μm) and a few small size Al2O3 clusters (≤40 μm). The transition and end slabs have still mainly small size Al2O3 blocks, but appear few big size (≥ 100 μm) composite inclusions.
     正常坯夹杂主要为尺寸较小(≤30μm)的块状及少量簇群状Al2O3夹杂(≤40μm),交接坯及尾坯仍以较小尺寸的块状Al2O3夹杂为主,但存在极少量大于100μm的复合夹杂.
短句来源
更多       
  相似匹配句对
     Differentiation of Compound Mappings
     映射的微分
短句来源
     Compound Modification Asphalt Waterproof Materials
     改性沥青防水材料
短句来源
     MORPHOLOGY OF Al_2O_3 INCLUSION
     氧化铝夹杂的形态
短句来源
     Detecting Structural Inclusion with Impedance Boundary Using Electromagnetic Wave
     电磁波探测阻抗的夹杂
短句来源
     The Interaction Problem Between the Elastic Line Inclusions
     弹性线夹杂的相互干扰
短句来源
查询“复合夹杂”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  complex inclusions
Connection of radiation pressure with the scattering amplitude of complex inclusions in a perfect liquid
      
The more complex inclusions consisted of alternating shells of light and dark material with tiny dense granules embedded in the latter.
      
Additional data on complex inclusions evoked by wisteria vein mosaic virus in pea leaf cells
      
Large complex inclusions evoked by wisteria vein mosaic virus contain cylindrical inclusions, mostly pinwheels (and bundles) and rarely also scrolls and laminar inclusions.
      
Especially in the case of two "complex" inclusions it was found that the crack propagation mode is highly rate dependent.
      
更多          


The morphology and composition of sulfide inclusions in pipeline steel were analyzed systematically.The effect of calcium treatment was also evaluated according to modification index of oxide and sulfide.After the calcium treatment,no manganese sulfide in grain boundaries was observed.The small amount of sulfide were classified into three types,(Ca,Mn)S complex inclusions,CaO-Al_2O_3-CaS,in which the CaS is uniformly dispersed,and CaO-Al_2O_3-CaS,in which the CaS is appeared as a distinct phase around the nuclei.These...

The morphology and composition of sulfide inclusions in pipeline steel were analyzed systematically.The effect of calcium treatment was also evaluated according to modification index of oxide and sulfide.After the calcium treatment,no manganese sulfide in grain boundaries was observed.The small amount of sulfide were classified into three types,(Ca,Mn)S complex inclusions,CaO-Al_2O_3-CaS,in which the CaS is uniformly dispersed,and CaO-Al_2O_3-CaS,in which the CaS is appeared as a distinct phase around the nuclei.These inclusions are beneficial to improvement of HIC resistance.Under current technology,the adding 0.7 kg/t calcium-silicon wire is not enough to modify,the inclusions,thus Ca-Si wire consumption should be increased appropriately.

系统分析了硫化物夹杂形貌、组成,并采用氧化物变性指标及硫化物变性指标对管线钢钙处理效果进行了全面评价,分析结果表明:管线钢经过钙处理后,没有发现沿晶界分布的MnS塑性夹杂,少量的硫化物夹杂由(Ca,Mn)S夹杂、CaS均匀分布的CaO-Al2O3-CaS复合夹杂和内核为CaO-Al2O3外壳为CaS的复合夹杂组成,这对于提高钢板抗HIC性能非常有利;在现有工艺条件下,硅钙线加入量为0.7 kg/t时夹杂物变性效果不理想,应适当增加硅钙线的加入量。

Inclusions and total oxygen content in ultra-low carbon(ULC) steel were studied for the control of cluster inclusions in ULC steel.Al_2O_3 and Al_2O_3-TiN are main inclusions in the steel.The size of most individual inclusions is less than 10 μm.When the total oxygen in slab is less than 0.0030%,there still exist cluster Al_2O_3 inclusions in the steel.The content of cluster Al_2O_3 inclusions is not in proportion with the total oxygen directly,therefore the content of inclusions in slab is not stood for by...

Inclusions and total oxygen content in ultra-low carbon(ULC) steel were studied for the control of cluster inclusions in ULC steel.Al_2O_3 and Al_2O_3-TiN are main inclusions in the steel.The size of most individual inclusions is less than 10 μm.When the total oxygen in slab is less than 0.0030%,there still exist cluster Al_2O_3 inclusions in the steel.The content of cluster Al_2O_3 inclusions is not in proportion with the total oxygen directly,therefore the content of inclusions in slab is not stood for by total oxygen in the steel totally.The cluster Al_2O_3 inclusions are related with oxygen activity after RH decarburization.In order to control cluster Al_2O_3 inclusions in ULC steel,it is necessary to control steelmaking process,including control of oxygen activity after RH decarburization and restriction of RH-OB with Al addition for heating.

为控制超低碳钢中的簇状夹杂物,对超低碳钢中的夹杂物和与全氧含量的关系进行了研究。钢中的夹杂物主要是Al2O3夹杂和Al2O3-TiN复合夹杂,独立夹杂物尺寸大部分小于10μm。铸坯中w(TO)小于0.003 0%时,钢中仍存在簇状Al2O3夹杂;Al2O3簇状夹杂物与铸坯中全氧含量没有直接关系,所以钢中的全氧含量不能完全代表钢中夹杂物的水平。钢中的簇状Al2O3夹杂物与RH脱碳结束活度氧有关,要控制超低碳钢中簇状Al2O3夹杂物必须稳定生产工艺,减少RH加铝升温,使RH脱碳结束活度氧保持在一定范围。

>=In this experimental research, SiCaBa wire was fed into cool heading steel in order to find out the effect on inclusion modification and total oxygen content, and SiCa wire was also fed as contrastive deoxidizer. The experimental findings showed that feeding SiCaBa wire had better effect on inclusion modification and decreasing total oxygen content than feeding SiCa wire Moreover, inclusion components changed from Al2O3 into mCaO· nAl2O3 or compound inclusions consisting of CaO, Al2O3 and SiO2 and morphology...

>=In this experimental research, SiCaBa wire was fed into cool heading steel in order to find out the effect on inclusion modification and total oxygen content, and SiCa wire was also fed as contrastive deoxidizer. The experimental findings showed that feeding SiCaBa wire had better effect on inclusion modification and decreasing total oxygen content than feeding SiCa wire Moreover, inclusion components changed from Al2O3 into mCaO· nAl2O3 or compound inclusions consisting of CaO, Al2O3 and SiO2 and morphology of inclusions changed into globular shape, accordingly, the capabilities of steel would be improved.

本实验以冷镦钢为实验钢种,在Al和FeSiAl脱氧之后喂SiCaBa包芯线,并以喂SiCa包芯线作为比较实验,以此研究喂SiCaBa线对夹杂物变性控制和全氧含量的影响。结果表明,喂SiCaBa线效果优于喂SiCa包芯线,钢中的全氧含量和夹杂物面积均有所降低,而且脱氧产物由Al2O3转变为mCaO·nAl2O3或者CaO-Al2O3-SiO2复合夹杂,从形貌上看近乎完全球化,对于提高钢材质量具有很大意义。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关复合夹杂的内容
在知识搜索中查有关复合夹杂的内容
在数字搜索中查有关复合夹杂的内容
在概念知识元中查有关复合夹杂的内容
在学术趋势中查有关复合夹杂的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社