anodizing film
相关语句
  阳极氧化膜
     Effect of Electrolytic Colouring on the Sealing Quality of the Aluminium Anodizing Film
     电解着色对铝阳极氧化膜封闭质量的影响
短句来源
     A coloring process for aluminum anodization is studied in mixed electrolytes containing oxalic acid,boric acid and sulfosolicylic acid respectively. The results show that a yellow,grey or champagne anodizing film can deposit on aluminum surface at 20~60(°C),50~60 V,which has a good corrosion resistance.
     分别采用草酸、硼酸和磺基水杨酸为主盐的复合电解液对铝进行阳极氧化着色研究,结果表明:当电压控制在50~60V,溶液温度20~60°C时,可在铝表面形成一层黄色、灰色或香槟色系的阳极氧化膜,氧化膜具有优异的耐蚀性能;
短句来源
     The surface of anodizing film have homogeneous distributions of small holes and good combination between the film and matrix alloy is found by SEM.
     用SEM对阳极氧化膜表面形貌和横截面形貌进行了观察,发现氧化膜表面形成了均匀孔洞,且与基体金属有很好的结合,并对此作出了合理的分析。
短句来源
     Influence of Addition Agents on Aluminium Foil a. c. Anodizing Film Property
     添加剂对铝箔交流阳极氧化膜性能的影响
短句来源
     EFFECTS OF RARE-EARTH SALTS ON PROPERTIES OF ANODIZING FILM OF ALUMINUM ALLOY
     铈盐和镧盐对铝合金阳极氧化膜性能的影响
短句来源
更多       
  氧化膜
     Preparation of Al_2O_3-PTFE Composite Anodizing Film on Al by High Voltage Anodization
     铝高压阳极氧化制备Al_2O_3-PTFE复合氧化膜
短句来源
     The thickness of the obtained anodizing film was up to 107 μm, and hardness was 480 kg/mm.
     所得氧化膜厚度高达107μm,硬度(HV)为480kg/mm。
短句来源
     Moreover, the anodizing film was composed of Al_ 2SiO_ 5, MgF_ 2, and MgAl_ 2O_ 4, and showed much better corrosion resistance than the same anodizing film prepared using conventional Cr-containing DOW17 process.
     氧化膜层主要由Al2SiO5、MgF2和MgAl2O4相组成; 氧化膜层的耐蚀性明显优于传统含铬DOW17工艺所得氧化膜层的耐蚀性。
短句来源
     Pulse anodizing process at high current density for ZL109 aluminium alloy was studied. The influences of H_2SO_4 concentration, malic acid, pulse current density, temperature and voltage on the thickness of anodizing film were discussed. Hence, the optimum process conditions were determined.
     研究了ZL109铝合金在大电流密度下的脉冲阳极氧化工艺,讨论了H2SO4浓度、苹果酸、脉冲电流密度、温度、电压对氧化膜厚度的影响,由此确定了最佳工艺条件。
短句来源
     The thickness of the hard anodizing film was 3~4 times as others, the highest thickness was up to 107μm and the micro-hardness was 350 ~ 600 HV. The oxidation temperature was improved up to room temperature by adding addition agent.
     采用氧化槽与活塞内外冷却的复合冷却方式的氧化条件下生成的硬质氧化膜厚度是目前阳极氧化方法的3~4倍,膜厚可达107μm,硬度HV为350~600。
短句来源
更多       
  阳极化膜
     :The pitting behaviour of the 7075-T6 Al alloy-anodizing film in NaCl solution has been studied by the immersion methodpotential change has been investigated during the degradation of anodizing film by measuring free corrosion potential of metal electrode,year corrosion rates have been calculated by weight-loss method and corrosion resistance of anodizing film has been evaluated .The result shows that local damage caused by Cl- on the film is very serious.
     利用浸渍法研究了7075-T6铝合金阳极化膜在Nacl介质中的小孔腐蚀行为,借助金属电极自腐蚀电位测量方法研究了阳极化膜失效期间的电位变化,通过失重计算出年腐蚀速率,从而评价了阳极氧化膜的耐蚀性能。 结果表明:Cl-对膜的局部破坏作用非常严重。
短句来源
  “anodizing film”译为未确定词的双语例句
     Surface treatment of AZ91D magnesium alloy by aluminum diffusion on anodizing film
     AZ91D镁合金阳极氧化与热扩散渗铝复合膜层的研究
短句来源
     The anodizing film obtained at the optimal conditions had porous structure, and the pores uniformly distributed in the film had an averaged size about 1~2 μm.
     在最佳工艺下所得阳极氧化膜层呈多孔结构,孔洞分布比较均匀,孔径尺寸约为1~2μm;
短句来源
     The function of K_2SiO_3 in anodic oxidation is to change the composition of anodizing film and form by XRD.
     经X射线衍射(XRD)分析发现,K2SiO3在阳极氧化中的作用主要是改变阳极氧化膜的成份;
短句来源
     The synergistic fluoropolymer self\|lubrication coatings on the aluminum hard anodizing film was studied.
     研究了铝及铝合金硬质阳极氧化协合含氟聚合物自润滑涂层技术。
短句来源
     Corrosion test results show that the composite coating by anodizing and aluminum diffusion has better corrosion protection for the AZ91D Mg alloy than the single anodizing film.
     AZ91D镁合金表面的阳极氧化和热扩散渗铝复合膜层能显著提高镁合金基体材料的耐腐蚀性能.
短句来源
更多       
查询“anodizing film”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


The purpose of this paper is mainly to discuss the ambient temperature sealing technology and to study the primery mechanizm of sealing the anodizing film of aluminium and its alloys.

本文主要论述铝及铝合金阳极氧化常温封闭工艺,并对封闭膜层的机理进行了初步的探讨。

Alternating electrolytic colouring of Al and its alloys is a recently popularized process succeeding dye absorption method. Close attention has been paid to it because of its excellent characteristices of colour homogeneity and sunlight resistance with low cost, high efficiency and simple equipment. In connection with troubles in present production, lustre and chromatism of anodizing film, stability of electrolytic colouring bath and so on are discussed on the basis of massive production practice for more...

Alternating electrolytic colouring of Al and its alloys is a recently popularized process succeeding dye absorption method. Close attention has been paid to it because of its excellent characteristices of colour homogeneity and sunlight resistance with low cost, high efficiency and simple equipment. In connection with troubles in present production, lustre and chromatism of anodizing film, stability of electrolytic colouring bath and so on are discussed on the basis of massive production practice for more than three years. (p.13—15)

铝及其合金的交流电解着色是继染料吸附法以后流行的最新工艺。由于具有优异的着色均匀性和耐晒性,成本低,生产效率高,设备简单,引起人们的关注。本文针对目前生产上存在的实际问题,总结三年多大槽生产经验,对氧化膜的色泽与色差控制,电解着色液的稳定性等方面进行了讨论。

The aluminium anodizing films with florid and even green, purple and tangerin colours were obtained in this investigation by controlling the wave shape of electric power by a microcomputer. The hardness, anticorrosion performance and the colour changing of the films after being sealed in boiling water were also studied.

利用微机控制铝阳极氧化电源的波形,获得了色泽鲜艳均匀的绿色、紫色、桔红色电解着色铝氧化膜。对它们的硬度、耐热性、耐蚀性及封孔后颜色的变化进行了研究。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关anodizing film的内容
在知识搜索中查有关anodizing film的内容
在数字搜索中查有关anodizing film的内容
在概念知识元中查有关anodizing film的内容
在学术趋势中查有关anodizing film的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社