    The key of melt-foaming is control cell size and bubble distributing uniformity in melt.
    熔体发泡法中关键的问题在于控制气泡大小以及气泡在铝液中分散的均匀性。
    Control of Mean Particle Size of Rare Earth Oxalate in Precipitation Process
    稀土草酸盐沉淀过程中颗粒大小的控制
短句来源
    Control of the particle shape and size in the process of precipitation of ultrafine nickel oxalate
    超细草酸镍沉淀过程中颗粒大小及形貌控制
短句来源
    Sheet zinc powder with suitable size and morphology is the most important material of zinc-chromium coating(DACRO), often prepared by ball milling or rubbing method, which is a products with high technology and high profits.
    片状锌粉是达克罗涂覆液中最重要的原料。 达克罗要求的锌粉是片状的金属粉末,它对锌粉的大小和形貌都有特殊的要求,并要经过表面改性后球磨或研磨制得,所以片状锌粉的制备技术是一种高技术含量,附加值相对较高的金属粉体制备技术。
短句来源
    The results show that good green compacts of cemented carbide could be made if the volume flow velocity is selected 60cm3/s when the wall temperature and the injection temperature are set at 300K and 400K respectively with lateral injecting inlet in size of 4 x1 mm2, which was proved by the experiments.
    模拟结:果表明:当采用大小为4×1mm~2的侧面浇口、模温320K、注射温度400K以及体积流速60cm~3/s的注射参数进行注射时可以得到良好无缺陷的硬质合金Ⅰ型拉伸试样预成形坯。
短句来源
更多       
  尺寸
    THE PROPERTIES OF Fe-P-C-Cu SYSTEM ALLOYS AND THEIR SIZE SHRINKAGE AFTER SINTERING
    Fe-P-C-Cu系合金的性能及其烧结后的尺寸收缩
短句来源
    Study of Crystal Size and Microstrain by Mechanical Alloying on Fe_(70)B_(30) Powder
    机械合金化过程中Fe_(70)B_(30)粉末晶粒尺寸和微观应变的研究
短句来源
    Influence of Preparation Conditions on Particle Size Distribution of ZrO 2 Ultrafine Powders
    制备条件对ZrO_2超细粒子尺寸及分布的影响
短句来源
    CHANGE OF CRYSTALLITE SIZE AND LATTICE DISTORTION INDUCED BY MECHANICAL ALLOYING IN Mo-37.5% POWDER MIXTURE
    机械球磨过程中Mo-37.5%Si混和粉晶粒尺寸和微观应变的研究
短句来源
    Magnet possessed a Br of 1.04 T and a JHc of 220 kA/m under the optimal sintering condition, and its microstructure contained satisfied grains with an average size of about 20 nm.
    在最佳烧结条件下得到磁体的磁性能为Br=1.02T,JHc=220kA/m。 磁体具有较好的微观结构,平均晶粒尺寸为20nm。
短句来源
更多       
  
    A mass of fine Al2O3parti-cles are dispersed in the copper base,the size of Al2O3particles is about 10~20 nm in diameter,and the spatial distance between particles is about 25~60 nm.
    同时Cu-Al合金颗粒完成了内氧化,生成了大量粒状的Al2O3并弥散分布于铜基体,其粒约为5~20 nm,颗粒间距约为25~60 nm。
短句来源
    The ultrafine nickel powders are prepared by polyol reduction process with NaOH, Ni(NO3)2·6H2O,ethylene glycol(EG) and polyvinylpyrrolidone(PVP) as raw materials,and the effects of precursor on particle size and morphology of nickel powders are investigated.
    采用Ni(NO3)2.6H2O、NaOH、乙二醇(EG)和聚乙烯吡咯烷酮(PVP)为原料,用多元醇法制备超细镍粉,研究前驱体对产物粒和形貌的影响。
短句来源
    In this experiment,the value of T [O] in AlMg1~# is 33.77 ppm and the effect of deasulfurization is obvious,the grain size of the inclusion is decreased by different dregrees.
    实验中AlMg1~#的T_([O])最低达到33.77ppm,脱硫效果明显; 铝镁合金脱氧后夹杂物的粒不同程度减少。
短句来源
    It is found that high-purity TiC-C compound powders can be prepared under vacuum condition whose size is <0.5μm with uniform distribution.
    研究结果表明,在真空条件下可合成出纯度较高的TiC-C复合粉体,其粒小于0.5μm。
短句来源
    Well dispersed α-Al2O3 powders with regular hexagonal platelike shape, small size of 1 μm was obtained by calcination of commercial gibbsite powders of 1 u m in sizes with addition of 2.5 wt% nano-sized α-Fe2O3 and 5 wt% NH4F.
    在平均粒度为1μm的工业氢氧化铝粉体中添加W(纳米α-Fe2O3)=2.5%和W(NH4F)=5%,经1100℃煅烧1h得到粒1 μm左右的六角片状α-Al2O3,粉体粒度均匀,分散性良好。
更多       
  粒径
    A mass of fine Al2O3parti-cles are dispersed in the copper base,the size of Al2O3particles is about 10~20 nm in diameter,and the spatial distance between particles is about 25~60 nm.
    同时Cu-Al合金颗粒完成了内氧化,生成了大量粒状的Al2O3并弥散分布于铜基体,其粒径约为5~20 nm,颗粒间距约为25~60 nm。
短句来源
    The ultrafine nickel powders are prepared by polyol reduction process with NaOH, Ni(NO3)2·6H2O,ethylene glycol(EG) and polyvinylpyrrolidone(PVP) as raw materials,and the effects of precursor on particle size and morphology of nickel powders are investigated.
    采用Ni(NO3)2.6H2O、NaOH、乙二醇(EG)和聚乙烯吡咯烷酮(PVP)为原料,用多元醇法制备超细镍粉,研究前驱体对产物粒径和形貌的影响。
短句来源
    In this experiment,the value of T [O] in AlMg1~# is 33.77 ppm and the effect of deasulfurization is obvious,the grain size of the inclusion is decreased by different dregrees.
    实验中AlMg1~#的T_([O])最低达到33.77ppm,脱硫效果明显; 铝镁合金脱氧后夹杂物的粒径不同程度减少。
短句来源
    It is found that high-purity TiC-C compound powders can be prepared under vacuum condition whose size is <0.5μm with uniform distribution.
    研究结果表明,在真空条件下可合成出纯度较高的TiC-C复合粉体,其粒径小于0.5μm。
短句来源
    Well dispersed α-Al2O3 powders with regular hexagonal platelike shape, small size of 1 μm was obtained by calcination of commercial gibbsite powders of 1 u m in sizes with addition of 2.5 wt% nano-sized α-Fe2O3 and 5 wt% NH4F.
    在平均粒度为1μm的工业氢氧化铝粉体中添加W(纳米α-Fe2O3)=2.5%和W(NH4F)=5%,经1100℃煅烧1h得到粒径1 μm左右的六角片状α-Al2O3,粉体粒度均匀,分散性良好。
更多       

 

查询“size”译词为其他词的双语例句

 

查询“size”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  size
The method we use is a combination of the smoothing effect of the operator ?t + ?x(2j+1) and a gauge transformation performed on a linear system, which allows us to consider initial data with arbitrary size.
      
We observe that our methods clearly show that the restriction p>amp;gt;2n/n+1 is closely related to cancellation and size properties of the gradient of the Poisson kernel.
      
Spaces called Sv were introduced by Jaffard [16] as spaces of functions characterized by the number ? 2ν(α)j of their wavelet coefficients having a size ? 2-αj at scale j .
      
In the examples, we obtain optimal bi-frames, i.e., primal and dual wavelets are constructed from a single fundamental refinable function, whose mask size is minimal w.r.t.
      
Transfersomes were prepared by reverse phase evaporation method and they were evaluated for shape, size, entrapment efficiency and deformability index.
      
更多          


点击这里查询相关文摘
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关size的内容
在知识搜索中查有关size的内容
在数字搜索中查有关size的内容
在概念知识元中查有关size的内容
在学术趋势中查有关size的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社