     An Analysis on Formation of ANF-6 Electroslag Fluxes Skin of Electroslag Remelting Ingot
     电渣重熔锭ANF-6熔渣渣皮形成的分析
短句来源
  相似匹配句对
     skin
     皮肤
短句来源
     Bioartificial skin
     人造生物皮肤
短句来源
     An Analysis on Formation of ANF-6 Electroslag Fluxes Skin of Electroslag Remelting Ingot
     电渣重熔锭ANF-6熔渣渣皮形成的分析
短句来源
查询“fluxes skin”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


The analysis on ingredient and petrographic examination of 5 mm thickness ANF-6 electroslag fluxes (70%CaF 2, 30%Al 2O 3) skin formed during 0.45C steel 260 kg ingot remelting by electroslag remelting furnace with 160 kW, Φ100 mm×350 mm mould indicated that the lamination phenomenon of fluxes was observed, and the Al 2O 3 content in fluxes skin near mould side and near electroslag ingot side was higher - 69.24%~75.62%, and the CaF 2 content was 21.46%~28.36%, where at skin center 3 mm location,...

The analysis on ingredient and petrographic examination of 5 mm thickness ANF-6 electroslag fluxes (70%CaF 2, 30%Al 2O 3) skin formed during 0.45C steel 260 kg ingot remelting by electroslag remelting furnace with 160 kW, Φ100 mm×350 mm mould indicated that the lamination phenomenon of fluxes was observed, and the Al 2O 3 content in fluxes skin near mould side and near electroslag ingot side was higher - 69.24%~75.62%, and the CaF 2 content was 21.46%~28.36%, where at skin center 3 mm location, the Al 2O 3 content in flux skin was only 15.84% and the CaF 2 content was 81.06%. The solidification mechanism of "ring shaped miniature fluxes pool" formed at upper edge of remelted ingot is advance in this paper, and the surface quality of ingot by using large over-cooling and low melting-point fluxes is higher than that by using low over-cooling and high melting-point fluxes.

在 16 0kW ,Φ10 0mm× 35 0mm结晶器电渣炉对 4 5钢 2 6 0kg锭重熔过程中形成的 5mm厚ANF 6熔渣 (70 %CaF2 +30 %Al2 O3 )渣皮成分和岩相分析表明 ,渣皮有分层现象 ,靠近结晶器一侧和靠近电渣锭一侧渣皮中的Al2 O3 含量较高 ,为 6 9 2 4 %~ 75 6 2 % ,CaF2 为 2 1 4 6 %~ 2 8 36 % ,渣皮中心 3mm处Al2 O3 含量仅为15 84 % ,CaF2 含量为 81 0 6 %。提出重熔锭上周缘形成“环形小熔池”的熔渣凝固机理 ;采用过冷度大 ,熔点低的熔渣所重熔的电渣钢锭的表面质量比采用熔点高、过冷度小的熔渣的电渣锭表面质量高。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关fluxes skin的内容
在知识搜索中查有关fluxes skin的内容
在数字搜索中查有关fluxes skin的内容
在概念知识元中查有关fluxes skin的内容
在学术趋势中查有关fluxes skin的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社