冷成形性
相关语句
  cold formability
     Cold Formability of Titanium(TAl) Sheet Used for Heat Exchanger
     换热器用纯钛TAl薄板冷成形性
短句来源
     Cold formability of titanium(TAl) sheet used for heat exchanger has been studicd. Tensile properties(σ_b,σ_(0.2),δ_5,n,r) have been tested, and erichsen, deep drawability and expanding tests have been done at the same time.
     通过测试拉伸性能(σ_b,σ_(0.2),δ_5,n,r)的方法,研究了换热器用纯钛TAl薄板的冷成形性,同时进行了杯突、拉深、扩孔试验,结果表明,n值与杯突值有很好的正相关性。
短句来源
     The effects of aluminium and oxygen elements on the mechanical properties and cold formability of the Ti-15-3 titanium alloy have been studied,this artical also gives the range of chemical composition control which provides basis for stable indusity production of the alloy.
     研究了铝和氧对Ti-15-3钛合金的力学性能和冷成形性能的影响,提出了该合金的成分控制范围,为该合金的工业化稳定生产提供了依据。
短句来源
     The effects of cold processing on ageing properties of the Ti-15-3 alloy have been studied,the cold formability and manufacturing processes of parts of this alloy have also been investigated,which provides experiences for the applications of sheet metal parts of the Ti-15-3 high strength titanium alloy.
     研究了冷加工对Ti-15-3合金时效性能的影响,并研究了该合金的冷成形性能及零件制造工艺,为Ti-15-3高强钛合金钣金零件的应用提供了经验。
短句来源
     The industrial test has shown that the truck beam(A610L) has not only the higher strength but also a good combination of strength and ductility as well as excellent cold formability,which are suitable to the higher requirement of truck beam performance for developing heavy duty trucks in the truck manufacture plant.
     工业生产试验表明:A610L不仅具有较高的抗拉强度,而且具有良好的强韧性和优异冷成形性能,满足了汽车厂开发重型载货车对汽车大梁板性能的要求。
短句来源
  cold forming
     Heat Treatment and Cold Forming Properties of β-21S Titanium Sheet
     β-21S钛合金薄板材的热处理工艺和冷成形性能研究
短句来源
     The analysis indicated that the developed Nb-Ti micro-alloying plate has the outstanding toughness,cold forming performance and good welding performance,which completely satisfied the requests of automotive vehicles and semi-trailers.
     分析结果表明,开发的含Nb-Ti钢带具有优异的韧性、冷成形性能和良好的焊接性能,完全满足汽车、半挂车用钢的要求。
短句来源
     The analysis indicated that the developed Nb-Ti micro-alloying plate has the outstanding toughness,the cold forming performance and the good welding performance,which completely satisfied with the request of automobile and semi-trailer.
     分析结果表明,开发的含Nb-Ti钢带具有优异的韧性、冷成形性能和良好的焊接性能,完全满足汽车、半挂车用钢的要求。
短句来源
     The analysis indicated that the developed Nb-Ti micro-alloying plate has the outstanding toughness, the cold forming performance and the good welding performance, which completely satisfied with the request of automobile and semi-trailer。
     分析结果表明,开发的含Nb-Ti钢带具有优异的韧性、冷成形性能和良好的焊接性能,完全满足汽车、半挂车用钢的要求。
     By the research on forging and cold forming performance of electromagnetism pure iron,the rational forging process is brought forth,it is specially emphasized to avoid the red brittleness and blue brittleness forging temperature range for the electromagnetism pure iron .
     通过对电磁纯铁锻造与冷成形性能的分析研究,给出了合理的锻造工艺,特别强调了要避开电磁纯铁的红脆与兰脆锻造温度区域。
短句来源
更多       
  cold formation
     Forging of Electromagnetism Pure Iron and Performance Research on Cold Formation
     电磁纯铁的锻造及冷成形性能研究
短句来源
  “冷成形性”译为未确定词的双语例句
     The high strength, high plasticity, low yield ratio, good continuous yielding property and good cold machinability of the dual phase steel(ML07SiZB) thus produced bycontrolled rolling and cooling speed render it a better cold-forming property.
     控轧—控冷双相钢(ML07Si 2B)具有高强度、高塑性、低屈服比、连续屈服、高的冷加工能力,因此具有优良的冷成形性
短句来源
     By accelerated cooling at rate of 8 ℃/s to 620 ℃ and slow cooling in furnace to simulate the coiling process, microstructure containing PF+AF+P, good bending formability, low ratio of yield strength to tensile strength were obtained for microalloyed lowcarbon Mn-B steel with tensile strength of 490 MPa. 
     轧后以平均冷速8℃/s快冷至620℃装炉缓冷模拟卷取,抗拉强度达到490MPa,显微组织由多边形铁素体+针状铁素体和少量珠光体构成,具有良好的冷成形性和较低的屈强比。
短句来源
查询“冷成形性”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  cold formability
The cold formability also exhibited a grain size dependence, with the Fe-11Al alloy with a fine recrystallised grain size having good cold rollability.
      
Critical embrittling strain rates at room temperature are in the range common to conventional metal-forming operations for the poorly processed alloy, and thus cold formability devolves importantly on initial processing.
      
Assessment of the Cold Formability of Ferritic Steels Using Parameters Determined in Uniaxial Tensile Testing
      
Possibilities and limits of the uniaxial tensile testing in the assessment of cold formability of ferritic low alloy steels are evaluated in the paper.
      
Cold formability covering both sheet and massive forming, including entire formability maps, strain hardening etc., can be estimated from six material parameters determined in a uniaxial tensile test.
      
更多          
  cold forming
The spheroidizing heat treatment is normally required prior to the cold forming in GCr15 steel in order to improve its machinability.
      
Influence of material flow constraints during cold forming on the deformation and densification behaviour of hypoeutectoid P/M s
      
Both carbon content and initial sintered ring geometry are also found to influence the deformation as well as densification rates during the cold forming process.
      
The carbide layers are adherent to the substrate and do not exfoliate in severe service as in cold forming.
      
Softening high hardenability steels for machining and cold forming
      
更多          
  cold formation
The experimental results thus indicate the cold formation of the reaction products.
      


Cold formability of titanium(TAl) sheet used for heat exchanger has been studicd. Tensile properties(σ_b,σ_(0.2),δ_5,n,r) have been tested, and erichsen, deep drawability and expanding tests have been done at the same time. It is proved that the n-Value has a direct relationship to IE-Value. The influence of oxygen contents to mechanical properties has been discussed.

通过测试拉伸性能(σ_b,σ_(0.2),δ_5,n,r)的方法,研究了换热器用纯钛TAl薄板的冷成形性,同时进行了杯突、拉深、扩孔试验,结果表明,n值与杯突值有很好的正相关性。σ_(0.2),n,r值各向异性较大。文章还讨论了氧含量对力学性能的影响。

The dual phase steel which contains 80% ferrite and 20% martensite can be produced by controlling the rolling within the dual phase area (α+γ) and the cooling speed after rolling.The high strength, high plasticity, low yield ratio, good continuous yielding property and good cold machinability of the dual phase steel(ML07SiZB) thus produced bycontrolled rolling and cooling speed render it a better cold-forming property. When useit as a cold upsetting steel to produce the high strength fasteners.the traditional...

The dual phase steel which contains 80% ferrite and 20% martensite can be produced by controlling the rolling within the dual phase area (α+γ) and the cooling speed after rolling.The high strength, high plasticity, low yield ratio, good continuous yielding property and good cold machinability of the dual phase steel(ML07SiZB) thus produced bycontrolled rolling and cooling speed render it a better cold-forming property. When useit as a cold upsetting steel to produce the high strength fasteners.the traditional hardening and tempering treatment can be elimi nated.

用双相区(α+γ)控制轧制和轧后控冷生产含(80%)铁素体+(20%)马氏体双相钢。控轧—控冷双相钢(ML07Si 2B)具有高强度、高塑性、低屈服比、连续屈服、高的冷加工能力,因此具有优良的冷成形性。作为冷镦钢生产高强度紧固件,可以省掉传统调质处理工艺。

The continuous cooling transformation (CCT) diagram for a microalloyed lowcarbon Mn-B steel was constructed by means of the combination of dilatometry and metallography. The simulation of controlled rolling, accelerated cooling and coiling processes was carried out on a 2high experimental mill and controllable cooling system. AF+PF is obtained at the cooling rates ranging from 10 to 25 ℃/s. By accelerated cooling at rate of 8 ℃/s to 620 ℃ and slow cooling in furnace to simulate the coiling process, microstructure...

The continuous cooling transformation (CCT) diagram for a microalloyed lowcarbon Mn-B steel was constructed by means of the combination of dilatometry and metallography. The simulation of controlled rolling, accelerated cooling and coiling processes was carried out on a 2high experimental mill and controllable cooling system. AF+PF is obtained at the cooling rates ranging from 10 to 25 ℃/s. By accelerated cooling at rate of 8 ℃/s to 620 ℃ and slow cooling in furnace to simulate the coiling process, microstructure containing PF+AF+P, good bending formability, low ratio of yield strength to tensile strength were obtained for microalloyed lowcarbon Mn-B steel with tensile strength of 490 MPa.

采用膨胀法结合金相分析建立微合金低碳Mn-B钢的动态CCT曲线,在二辊实验轧机和控冷设备上模拟热连轧、快速冷却及卷取工艺。实验结果表明:变形后以10~25℃/s的速度冷却,获得针状铁素体(AF)+多边形铁素体(PF)组织。轧后以平均冷速8℃/s快冷至620℃装炉缓冷模拟卷取,抗拉强度达到490MPa,显微组织由多边形铁素体+针状铁素体和少量珠光体构成,具有良好的冷成形性和较低的屈强比。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关冷成形性的内容
在知识搜索中查有关冷成形性的内容
在数字搜索中查有关冷成形性的内容
在概念知识元中查有关冷成形性的内容
在学术趋势中查有关冷成形性的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社