   epoxy-silicone 的翻译结果: 查询用时:0.05秒
图标索引 在分类学科中查询
所有学科
一般化学工业
更多类别查询

图标索引 历史查询
 

epoxy-silicone
相关语句
  环氧改性有机硅
     HEAT RESISTANCE AND CORROSION RESISTANCE OF EPOXY-SILICONE BASED COATING
     环氧改性有机硅涂料耐热耐蚀性研究
短句来源
     At the base of those, the epoxy-silicone resin of defferent proportions resins are synthesized by the condensation polymerization of the silicone oligomer with bisphenol A epoxy resin.
     通过对改性树脂合成反应的研究,查明了中间体与环氧树脂的配比、反应温度、时间及改性促进剂等因素的影响,在此基础上确定了环氧改性有机硅树脂的合成工艺:有机硅中间体与环氧树脂按4∶6到7∶3的质量,在130-170℃和改型促进剂的作用下,经3~5小时反应可得到环氧改性有机硅树脂。
短句来源
  环氧有机硅
     Heat Resistance of Anti-Corrosion Epoxy-Silicone Resin Coating
     环氧有机硅防腐蚀涂料耐热性的研究
短句来源
     Heat resistance and corrosion resistance of epoxy-silicone based coatings
     耐热和耐蚀的环氧有机硅涂料的研究
短句来源
     Synthesis of Epoxy-silicone Resin and Research of the Anti-corrosion Paint with High-temperature Vapor Tolerance
     环氧有机硅树脂的合成及耐高温蒸汽防腐涂料的研究
短句来源
  “epoxy-silicone”译为未确定词的双语例句
     ⑶ Copolymer epoxy-silicone resin was synthesized by using prepolymer oforganicsilica and epoxy resin as materials .
     ⑶以环氧树脂和有机硅树脂预聚体为原料,通过缩聚合成环氧-有机硅共聚树脂。
短句来源
     Epoxy-Silicone Resin Modified with Polyurethane Active Monomer
     活性聚氨酯单体改性环氧-有机硅树脂性能的研究
短句来源
     A heat insulation and anti-corrosive coatings is prepared from epoxy-silicone resin as film-forming substance and silicon dioxide of vitreous body,special ceramics,zinc phosphate and fibers as fillers.
     以环氧改性有机硅树脂作为成膜物质,并以玻璃体二氧化硅材料、特殊陶瓷材料、磷酸锌、纤维材料为填料,制成保温隔热防腐涂料。
短句来源
     As a result , the kind of epoxy-silicone coating is ofhighly heating-resistant property, and maximum temperature can be reached 900℃.
     结果表明,制备的环氧-有机硅耐高温涂料具有良好的耐高温性,最高可耐900℃的高温。
短句来源
     Study on Highly Heating-Resistant Coating of Epoxy-silicone Resin
     环氧—有机硅耐高温涂料的研制
短句来源
更多       
  相似匹配句对
     SOLVENTLESS EPOXY PAINT
     第六章 无溶剂型环氧涂料
短句来源
     Epoxy Tooling by Stereolithography
     基于光固化原型的环氧树脂制模技术
短句来源
     (4) epoxy-resin.
     ④环氧树脂。
短句来源
     PROGRESS OF EPOXY-NANOCOMPOSITES
     环氧树脂基纳米复合材料研究进展
短句来源
     Epoxy functional Polysilicone Emulsion
     含环氧基聚硅氧烷乳液的研究
短句来源
查询“epoxy-silicone”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  epoxy-silicone
Particulation of epoxy and epoxy-silicone classes of barrier with ultrafine SiC has revealed a more positive potential and lower galvanic currents.
      


Choosing polyurethane active monomer(TDI) as modifying reagent,the modification of epoxy-silicone resin is developed.The reaction happened in the materials is testified by means of IR.Several properties of products are discussed and the results show that the properties of modified resin are greatly improved,such as flexibility of film,adhesive power and anticorrosion

研究了活性聚氨酯单体TDI改性环氧 -有机硅树脂 (ES)的化学反应 ,并对改性产物的结构和性能进行了研究 ,结果表明 :改性后的树脂其成膜性以及成膜后的附着力、耐腐蚀性等性能得到明显改善

A heat resistance and anticorrosive coating was prepared with epoxy-silicone resin and ceramic powder of different particle size. The preparation and properties of heat resistance coating based on the epoxy-modified silicone were described, and the heat resistance of coating was assessed by thermogravimetric analysis (TGA) , electrochemical impedance spectrum (EIS) and scan electron microscope (SEM) . Results revealed that the coating could be cured at ambience temperature and had excellent heat resistance....

A heat resistance and anticorrosive coating was prepared with epoxy-silicone resin and ceramic powder of different particle size. The preparation and properties of heat resistance coating based on the epoxy-modified silicone were described, and the heat resistance of coating was assessed by thermogravimetric analysis (TGA) , electrochemical impedance spectrum (EIS) and scan electron microscope (SEM) . Results revealed that the coating could be cured at ambience temperature and had excellent heat resistance. The coating was still stable and had good corrosion resistance on the surface of mild steel up to 250℃ and would degrade only over the temperature. The failure mechanism of coating was also discussed.

采用环氧有机硅树脂与多种不同粒径陶瓷粉,研制出一种耐高温防腐蚀涂料。使用热重分析法、电化学交流阻抗法和电镜扫描对环氧有机硅涂料的耐热性进行了研究。试验结果表明,耐高温防腐蚀涂料可常温固化,具有较好的耐高温性能。涂层在钢表面达到250℃时是稳定的,具有良好的耐腐蚀效果,同时根据试验结果讨论了涂层的破坏机理。

This paper deals with the study of the external thermal insulation coating for a solid rocket motor (SRM) case. By comparing several materials, an epoxy silicone resin cured at room temperature is selected as the matrix of the coating.The solvent is a mixture of acetone and xylene.Tensile strength of the coating is above 7 MPa and tensile elongation is above 1%.Thermal conductivity,specific heat capacity and density of the coating is 0.221 W/(m·K), 1.72×10 3 J/(kg·K) and 1.256 g/cm 3 respectively.At the...

This paper deals with the study of the external thermal insulation coating for a solid rocket motor (SRM) case. By comparing several materials, an epoxy silicone resin cured at room temperature is selected as the matrix of the coating.The solvent is a mixture of acetone and xylene.Tensile strength of the coating is above 7 MPa and tensile elongation is above 1%.Thermal conductivity,specific heat capacity and density of the coating is 0.221 W/(m·K), 1.72×10 3 J/(kg·K) and 1.256 g/cm 3 respectively.At the same time, the coating′s capability of heat resistance, thermal insulation and adhesion are also very good.

介绍某固体发动机壳体外防热涂层的研究情况。通过各种基体材料的选择研究 ,确定所研制涂料由有机硅改性环氧树脂室温固化体系与耐热和隔热功能填料组成 ;溶剂为丙酮和二甲苯的混合物。涂层的拉伸强度≮ 7MPa ;伸长率≮ 1 % ;热导率为 0 .2 2 1W/ (m·K) ,比热容为 1 .72× 1 0 3J/ (kg·K) ,密度为 1 .2 5 6g/cm3;并具有较高的耐热性、隔热性和良好的附着力

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关epoxy-silicone的内容
在知识搜索中查有关epoxy-silicone的内容
在数字搜索中查有关epoxy-silicone的内容
在概念知识元中查有关epoxy-silicone的内容
在学术趋势中查有关epoxy-silicone的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社