     The results indicated that the average dynamic frictional coefficient (FC) of C/C composites was decreased in dry condition, but damp condition average dynamic FC and dry condition average static FC were increased as temperature was increased.
     结果表明:随着处理温度的升高,C/C复合材料的干态平均动摩擦系数由大变小,湿态平均动摩擦系数及干态平均静摩擦系数由小变大。
短句来源
     After C/C composites were treated under 2500℃,they had smooth brake process and small wear, and their average dynamic FC was slowly decreased in damp condition.
     经过2500℃处理的C/C材料,不仅刹车过程平稳,湿态平均动摩擦系数衰减少,而且磨损率小。
短句来源
     The average dynamic FC of four kinds of samples treated under different temperatures was reduced in dry and damp condition as brake pressure and energy were raised.
     当刹车比压和能载增加时,经过不同温度处理的四种试样干态及湿态平均动摩擦系数均相应下降。
短句来源
  相似匹配句对
     in average;
     平均为0.89d。
短句来源
     Dynamic
     地方科技动态
短句来源
     Fc?
     血管内皮细胞Fc?
短句来源
     DYNAMIC
     动态
短句来源
     Fc?
     Fc?
短句来源
查询“average dynamic fc”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


A description is given of the effect of high temperature treatment on tribological properties of carbon/carbon (C/C) composites prepared by chemical vapour deposition. The curve diagram of brake moment brake time of different temperature treated samples was analyzed. The results indicated that the average dynamic frictional coefficient (FC) of C/C composites was decreased in dry condition, but damp condition average dynamic FC and dry condition average static FC were increased...

A description is given of the effect of high temperature treatment on tribological properties of carbon/carbon (C/C) composites prepared by chemical vapour deposition. The curve diagram of brake moment brake time of different temperature treated samples was analyzed. The results indicated that the average dynamic frictional coefficient (FC) of C/C composites was decreased in dry condition, but damp condition average dynamic FC and dry condition average static FC were increased as temperature was increased. After C/C composites were treated under 2500℃,they had smooth brake process and small wear, and their average dynamic FC was slowly decreased in damp condition. The average dynamic FC of four kinds of samples treated under different temperatures was reduced in dry and damp condition as brake pressure and energy were raised.

研究了高温处理对化学气相沉积碳/碳(简称C/C)复合材料摩擦磨损性能的影响,分析了经过不同温度处理的试样的刹车力矩-刹车时间曲线。结果表明:随着处理温度的升高,C/C复合材料的干态平均动摩擦系数由大变小,湿态平均动摩擦系数及干态平均静摩擦系数由小变大。经过2500℃处理的C/C材料,不仅刹车过程平稳,湿态平均动摩擦系数衰减少,而且磨损率小。当刹车比压和能载增加时,经过不同温度处理的四种试样干态及湿态平均动摩擦系数均相应下降。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关average dynamic fc的内容
在知识搜索中查有关average dynamic fc的内容
在数字搜索中查有关average dynamic fc的内容
在概念知识元中查有关average dynamic fc的内容
在学术趋势中查有关average dynamic fc的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社