     STUDY ON CAUSE OF COLD BEND CRAZE AND PLASTICITY NON—ACCEPTABILITY OF CABLE CHAIN STEEL
     锚链钢冷弯开裂及塑性不合格原因研究
短句来源
     Analyzing on Transverse Fissure of Cable Chain Ring
     锚链环横裂原因分析
短句来源
     Percent of pass of cold bend and physical check of cable chain steel produced by this company was 99 4% in 1996 , 98 47%-in January~June of 1997. Investigation on cause of cold bend craze and plasticity nonacceptability of the steel was done. Results showed that main cause was to recarburize steel ingot face leased by shielding slag, other causes were too long heating time and high heating temperature of steel ingot in rolling, etc.
     涟钢锚链钢的冷弯和物检合格率 1996年为 99.4%,1997年上半年只有 98.47%,为此组织了专门的调查研究 ,发现保护渣使钢锭表面增碳是冷弯开裂的主要原因 ,轧钢加热时间过长或温度过高 ,试样的加工等也是影响因素。
短句来源
     After use of good quality control measure, percent of pass of cable chain steel was 100% in 1998.
     采取相应的措施后 ,1998年涟钢锚链钢的合格率达到 10 0 %。
短句来源
     This paper disccusses produced cause of transverse fissure at the time of ringed cable chain The examiration result has proved that the main reason produced transverse fissure is hot brittleness caused by higher content of harmful residual elements in steel For preventing the transverse fissure,Cu equivalence in steel must be controlled within the limits of 0 4%
     检验结果表明 ,锚链环横裂的主要原因是钢中残存有害元素较高引起的热脆所致。 为防止锚链弯环横裂 ,应控制钢中Cu当量不大于 0 4%。
短句来源
  相似匹配句对
     A chain cable for marine engineering
     海洋工程用的锚链
短句来源
     Analyzing on Transverse Fissure of Cable Chain Ring
     锚链环横裂原因分析
短句来源
     Chain of Immunology
     免疫链
短句来源
     Chain Management
     发展我国连锁经营的思考
短句来源
     Analyzed of Cable
     电缆行业现状分析
短句来源
查询“cable chain”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  cable chain
The transmission characteristics of the striplines are reasonably wellmatched in impedance to the rest of the cable chain.
      
The transmission characteristics of the striplines are reasonably well matched in impedance to the rest of the cable chain.
      
Light springs where used on the cable mechanism for opening opposed by heavy springs on the opening cable chain.
      


Percent of pass of cold bend and physical check of cable chain steel produced by this company was 99 4% in 1996 , 98 47%-in January~June of 1997. Investigation on cause of cold bend craze and plasticity nonacceptability of the steel was done. Results showed that main cause was to recarburize steel ingot face leased by shielding slag, other causes were too long heating time and high heating temperature of steel ingot in rolling, etc. After use of good quality control measure, percent of pass of cable...

Percent of pass of cold bend and physical check of cable chain steel produced by this company was 99 4% in 1996 , 98 47%-in January~June of 1997. Investigation on cause of cold bend craze and plasticity nonacceptability of the steel was done. Results showed that main cause was to recarburize steel ingot face leased by shielding slag, other causes were too long heating time and high heating temperature of steel ingot in rolling, etc. After use of good quality control measure, percent of pass of cable chain steel was 100% in 1998.

涟钢锚链钢的冷弯和物检合格率 1996年为 99.4%,1997年上半年只有 98.47%,为此组织了专门的调查研究 ,发现保护渣使钢锭表面增碳是冷弯开裂的主要原因 ,轧钢加热时间过长或温度过高 ,试样的加工等也是影响因素。采取相应的措施后 ,1998年涟钢锚链钢的合格率达到 10 0 %。

This paper disccusses produced cause of transverse fissure at the time of ringed cable chain The examiration result has proved that the main reason produced transverse fissure is hot brittleness caused by higher content of harmful residual elements in steel For preventing the transverse fissure,Cu equivalence in steel must be controlled within the limits of 0 4%

对锚链弯环时横向裂纹的产生原因进行了探讨。检验结果表明 ,锚链环横裂的主要原因是钢中残存有害元素较高引起的热脆所致。为防止锚链弯环横裂 ,应控制钢中Cu当量不大于 0 4%。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关cable chain的内容
在知识搜索中查有关cable chain的内容
在数字搜索中查有关cable chain的内容
在概念知识元中查有关cable chain的内容
在学术趋势中查有关cable chain的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社