hydrothermal annealing
相关语句
  水热烧结
     It conludes that under the condition of 30% of P25 powder content and hydrothermal annealing 12 hours in 100℃,the TiO_(2)porous thin film prepared exhibits good crystal structure,excellent light absorbance,and electric performance.
     结果表明:P25粉体添加量为30%,100℃水热烧结12 h,可以形成结晶良好,吸光度较好的TiO2多孔薄膜。
短句来源
  “hydrothermal annealing”译为未确定词的双语例句
     Preparation of TiO_2 thin film by hydrothermal annealing and its performance inspection
     水热制备TiO_2薄膜及其性能检测
短句来源
  相似匹配句对
     ANNEALING OF GLASS
     玻璃的退火
短句来源
     DETERMINISTIC ANNEALING
     确定性退火技术
短句来源
     ON HYDROTHERMAL ROCK
     关于热液岩
短句来源
     Hydrothermal Eruption
     水热爆炸
短句来源
     Preparation of TiO_2 thin film by hydrothermal annealing and its performance inspection
     水热制备TiO_2薄膜及其性能检测
短句来源
查询“hydrothermal annealing”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  hydrothermal annealing
The second annealing stage (the hydrothermal annealing stage) was performed at 300 MPa and 900-1050 ° C under a hydrogen fugacity of ~ 158 MPa for 1-5 h.
      
Hydrothermal annealing of fully metamict gadolinite at 710° C and PH2O=2.3 kbar resulted in direct recrystallization.
      
High albite-structure NaGaSi3O8, grown in a Na2WO4 flux, was ordered by hydrothermal annealing below 820° C and dry annealing above 820° C, to avoid melting, using a load pressure of approximately 1 kbar.
      
Approximately 125 hydrothermal annealing experiments have been carried out in an attempt to bracket the stability fields of different ordered structures within the plagioclase feldspar solid solution.
      


This paper describes the preparation of TiO_(2)porous thin film by sol-gel revolve method.Its performance in crystal structure,surface morphology,absorption spectrum,and electrical characteristics are inspecteded by X-ray,SEM,AFM,and UVSP.It conludes that under the condition of 30% of P25 powder content and hydrothermal annealing 12 hours in 100℃,the TiO_(2)porous thin film prepared exhibits good crystal structure,excellent light absorbance,and electric performance.

采用溶胶-凝胶旋转法制备TiO2多孔薄膜,用X-射线分析仪、扫描电镜、原子力显微镜,紫外-可见分光光度计,检测薄膜析晶分析、表面形貌、吸光度、电池的电性能。结果表明:P25粉体添加量为30%,100℃水热烧结12 h,可以形成结晶良好,吸光度较好的TiO2多孔薄膜。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关hydrothermal annealing的内容
在知识搜索中查有关hydrothermal annealing的内容
在数字搜索中查有关hydrothermal annealing的内容
在概念知识元中查有关hydrothermal annealing的内容
在学术趋势中查有关hydrothermal annealing的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社