    In term of design of welding seam,pressure in nozzle junctions,stress analysis and so on,this paper makes analysis on the cause of crack on the joint between the external circumference of reinforcing ring and cylinder of steam mixing distributor,and proposes that attention should be paid to thin kind of welding seam during design,manufacture,installation,operation and maintenance
    从焊接接头型式的设计、接管区的受力情况和应力分析等方面着手 ,分析了蒸汽混合分布器的接管补强圈外圆周与筒体连接的角焊缝出现裂纹的原因 ,并提出应在设计、制造、安装、使用管理等方面对这类焊缝加以重视。
短句来源
  相似匹配句对
    Analysis to Cracks on Pipe Angle Seam of Type Ⅲ Pressure Vessel
    Ⅲ类压力容器接管焊缝裂纹分析
短句来源
    Formation and Remediation of Cracks in the Angle Welding Joint of a Waste Heat Boiler of an Ethylene Plant
    裂解废热锅炉焊缝裂纹产生原因及解决措施
短句来源
    Preparation of wool's keratin solution
    羊毛蛋白质溶液的制备
短句来源
    STUDY ON THE CORROSION RESISTANCE OF POLYPROPYLENE WELDING LINE
    聚丙烯焊缝耐蚀性能研究
短句来源
    DAMAGE ANALYSIS OF SADDLE WELD IN THE OUTLET MANIFOLD
    下集气管马鞍焊缝的损伤分析
短句来源
查询“角焊缝”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


Abstract Lots of cracks were found in the base metal and weld during periodical inspection of the stable gasolin heat exchanger.The crack initiation cause involved in materials,welding,quality、stress、working medium was analyzed.The defect disposal method was probed in this paper.

前言1996年8月,某石油化工厂E303稳定汽油换热器因底部放空管的角焊缝部位泄漏而停车。对该容器进行内、外部全面检验发现母材和焊缝存在大量表面裂纹,经分析为应力腐蚀裂纹;对主体材质进行化学成分分析,发现硫含量严重超标;由于材料质量不合格,工作介质中...

The cause for the crack appearing on the angle welding joint of the lower feed water collector of a waste heat boiler in an ethylene plant,leading to intrusion of high pressure boiler feed water into low pressure cracking gas,was found to be the result o f alkali corrosion due to improper welding.To solve the problem,the welding joint construction was re-designed and argon-arc welding was employed.The result has been satisfactory.

针对乙烯装置废热锅炉给水下集合管连接角焊缝产生穿透性裂纹的事故 ,分析其原因为焊接不良而产生碱腐蚀。解决措施为采用氩弧焊 ,改进焊接结构设计等。改造后的废热锅炉运行良好。

In term of design of welding seam,pressure in nozzle junctions,stress analysis and so on,this paper makes analysis on the cause of crack on the joint between the external circumference of reinforcing ring and cylinder of steam mixing distributor,and proposes that attention should be paid to thin kind of welding seam during design,manufacture,installation,operation and maintenance

从焊接接头型式的设计、接管区的受力情况和应力分析等方面着手 ,分析了蒸汽混合分布器的接管补强圈外圆周与筒体连接的角焊缝出现裂纹的原因 ,并提出应在设计、制造、安装、使用管理等方面对这类焊缝加以重视。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关角焊缝的内容
在知识搜索中查有关角焊缝的内容
在数字搜索中查有关角焊缝的内容
在概念知识元中查有关角焊缝的内容
在学术趋势中查有关角焊缝的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社