optimal finishing process
相关语句
  最佳整理工艺
     At last, the optimal finishing process parameters arerevealed through the orthogonal experiment as follow: nano-structure finishing agentconcentration of 10g/L , bake time of 120 s, bake temperature of 150℃, immersed time of15 min and bath ratio of 1:30. Trough the treatment of this process, the averagetransmittance of ultraviolet ray at 280~320nm decrease 90.7% ,which improves greatlyanti-ultraviolet property of fabric.
     最终通过正交实验找到最佳整理工艺,:纳米整理剂用量为 10 g/L、焙烘时间 120s、焙烘温度 150℃、浸渍时间为 15min 以及浴比 1:30。 经过此工艺整理后,在 280-320nm 之间紫外线平均透过率减少了 90.7﹪而使整理后的织物抗紫外线性能大大提高。
短句来源
     The optimal finishing process parameters are revealed throughthe orthogonal experiment as follow: amino silicones concentration of 20g/L , chitosanconcentration of 0.5%, bake temperature of 140℃, bake time of 120 s.
     通过正交实验找到最佳整理工艺:氨基硅酮整理剂用量为 20g/L、壳聚糖浓度为 0.5%、焙烘温度为 140℃及焙烘时间 120s。
短句来源
     Quantitative analysis of the factors influencing the anti-pilling finishing of worsted and woollen fancy fabrics is performed through orthogonal experiment, and based on the results, variance analysis is undertaken to investigate the prominent influencing factors and the optimal finishing process is presented.
     采用正交分析法对影响精纺粗花呢抗起毛起球整理工艺因素进行了定量的分析,依据试验结果进行方差分析,讨论影响因素的显著性,提出精纺粗花呢抗起毛起球最佳整理工艺条件。 整理后的织物抗起毛起球效果显著,同时呈现出良好手感和风格。
短句来源
     The preparation,finishing mechanism and practical application of fragrant microcapsules are reviewed,elucidating the manufacture method of the fragrant textile. The optimal finishing process for fragrant nano-sizemicrocapsules is determined by experiments.
     介绍了香味微胶囊整理的机理、香味微胶囊的制备和应用实践,阐述了香味纺织品的生产方法,通过试验筛选出香味纳米微胶囊的最佳整理工艺
短句来源
  “optimal finishing process”译为未确定词的双语例句
     As a result,the optimal finishing process of cotton fabric was as follows: flame retardant 200~250 g/L,crosslinker 50~60 g/L,catalyst(magnesium chloride)20 g/L,softener 30 g/L,pH value 5~7,curing 2 min at 160~170 ℃.
     研究结果表明,该阻燃剂针对棉织物的优化整理工艺为:阻燃剂200-250 g/L,交联剂50-60 g/L,催化剂(氯化镁)20 g/L,柔软剂30 g/L,整理液pH值5-7,160-170℃焙烘2 m in。
短句来源
     Polycarboxylic acid-the copolymer(PMA) of maleic acid(MA) and itaconic acid(IA) was synthesized and applied to tussah silk for crease-proofing finish. The optimal finishing process was selected through orthogonal experiment. The results showed that the fabric treated with PMI had better wet elasticity, washing resistance with little influence on whiteness or fiber strength.
     合成马来酸(MA)、依康酸(IA)共聚物(PMI),用于柞丝绸的抗皱整理,通过正交试验优选了其在柞丝绸防皱整理中的应用工艺,结果表明:织物经PMI整理后,湿弹性显著提高,耐洗性较好,对织物的白度和强度基本无影响
短句来源
  相似匹配句对
     Optimal temperature for D.
     各种光强下的暗呼吸速率均随温度升高而增大。
短句来源
     It is the optimal pattern.
     这个结果如同自然界生态平衡一样,是相对最优的格局。
短句来源
     Aroma finishing
     芳香整理
短句来源
     Finishing of Lyocell
     Lyocell的整理(第三部分)
短句来源
     Optimal Model of Rolling Lot Scheduling for the Finishing Operation in Rolling Mill
     轧钢厂的精轧工序轧制批量调度的优化模型
短句来源
查询“optimal finishing process”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


Polycarboxylic acid-the copolymer(PMA) of maleic acid(MA) and itaconic acid(IA) was synthesized and applied to tussah silk for crease-proofing finish. The optimal finishing process was selected through orthogonal experiment. The results showed that the fabric treated with PMI had better wet elasticity, washing resistance with little influence on whiteness or fiber strength.

合成马来酸(MA)、依康酸(IA)共聚物(PMI),用于柞丝绸的抗皱整理,通过正交试验优选了其在柞丝绸防皱整理中的应用工艺,结果表明:织物经PMI整理后,湿弹性显著提高,耐洗性较好,对织物的白度和强度基本无影响

The crease-risist finishing of bamboo fabric by PMA was studied.The influence of PMA dosage,curing temperature and time on crease-resist effect of bamboo fabric was discussed.The optimal finishing process was obtained by testing the dry and wet crease recovery angles and the whiteness of fabrics treated under different conditions.The structure and properties of treated fabrics were studied by X-ray diffraction and infrared spectrum.The results show that the crosslinking reaction occurs between finishing...

The crease-risist finishing of bamboo fabric by PMA was studied.The influence of PMA dosage,curing temperature and time on crease-resist effect of bamboo fabric was discussed.The optimal finishing process was obtained by testing the dry and wet crease recovery angles and the whiteness of fabrics treated under different conditions.The structure and properties of treated fabrics were studied by X-ray diffraction and infrared spectrum.The results show that the crosslinking reaction occurs between finishing agent and macromolecule chains in the uncrystallized region of fibers,which improves heat stability,while the crystallized structure has little change.

以多元羧酸——聚马来酸(PMA)作为抗皱整理剂对竹纤维织物进行抗皱整理,讨论了整理剂用量、焙烘温度、焙烘时间对抗皱整理效果的影响,通过测试在不同整理条件下织物的折皱回复角、白度、断裂强力等性能取得了优化整理条件。整理后通过X-射线衍射和红外光谱对织物进行了一些结构和性能的测试,结果表明:整理剂在纤维无定形区大分子链之间发生了交联反应,提高了纤维的抗皱性能,纤维的晶区结构基本没有发生改变。

Quantitative analysis of the factors influencing the anti-pilling finishing of worsted and woollen fancy fabrics is performed through orthogonal experiment, and based on the results, variance analysis is undertaken to investigate the prominent influencing factors and the optimal finishing process is presented.

采用正交分析法对影响精纺粗花呢抗起毛起球整理工艺因素进行了定量的分析,依据试验结果进行方差分析,讨论影响因素的显著性,提出精纺粗花呢抗起毛起球最佳整理工艺条件。整理后的织物抗起毛起球效果显著,同时呈现出良好手感和风格。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关optimal finishing process的内容
在知识搜索中查有关optimal finishing process的内容
在数字搜索中查有关optimal finishing process的内容
在概念知识元中查有关optimal finishing process的内容
在学术趋势中查有关optimal finishing process的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社