     FAILURE ANALYSIS OF THE REDIRECTOR SCREW
     转向器螺杆失效分析
短句来源
     The crack in root of whorl of the redirector screw was analyzed by means of chemical composition analysis,microstructure examination and hardness testing .
     采用化学分析、金相检验和硬度测试等方法对转向器螺杆螺纹根部的裂纹进行了分析。
短句来源
  相似匹配句对
     FAILURE ANALYSIS OF THE REDIRECTOR SCREW
     转向器螺杆失效分析
短句来源
     Magnetic Screw
     磁力丝杠
短句来源
     The Development of Screw
     浅谈螺旋桨的发展趋势——螺旋桨的设计与应用正引起人们前所未有的关注
短句来源
     The crack in root of whorl of the redirector screw was analyzed by means of chemical composition analysis,microstructure examination and hardness testing .
     采用化学分析、金相检验和硬度测试等方法对转向器螺杆螺纹根部的裂纹进行了分析。
短句来源
     Discussing the formation of the swing of redirector and the solutions
     转向器摆振成因与消除方法探讨
短句来源
查询“redirector screw”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


The crack in root of whorl of the redirector screw was analyzed by means of chemical composition analysis,microstructure examination and hardness testing .The results showed that redirector screw was quenched insufficiency after cementite disposaled,internal stress of the accessory was immanence factor of the crack initiation. In addition, secondary induratial layer due to unseemliness grinding. The superficial grinding cracks was caused by the stress superposition which exceed the limitation...

The crack in root of whorl of the redirector screw was analyzed by means of chemical composition analysis,microstructure examination and hardness testing .The results showed that redirector screw was quenched insufficiency after cementite disposaled,internal stress of the accessory was immanence factor of the crack initiation. In addition, secondary induratial layer due to unseemliness grinding. The superficial grinding cracks was caused by the stress superposition which exceed the limitation of tensile strength of the material.

采用化学分析、金相检验和硬度测试等方法对转向器螺杆螺纹根部的裂纹进行了分析。结果表明,转向器螺杆渗碳处理及淬火后,螺杆表层产生高碳马氏体组织而其心部却未发生马氏体转变,引起零件内的组织应力增大,这是产生裂纹的内在因素,另外,磨削方法不当又产生了二次淬硬层,叠加的应力超过了材料的强度极限时,导致了钢件表面磨削裂纹的产生。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关redirector screw的内容
在知识搜索中查有关redirector screw的内容
在数字搜索中查有关redirector screw的内容
在概念知识元中查有关redirector screw的内容
在学术趋势中查有关redirector screw的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社