  低铬钝化
     Through SEM test, colour observation and corrosion resistance measurement in humid hot environment of passivation film on Zinc coating it is shown that structure of low chromium green black passivation film is finer than that of medium chromium green black passivation film. The corrosion resistance of low chromium passivation film is higher than that of medium chromium passivation film. The process of film formation is not linear relation but divided into two different stages.
     经SEM、钝化膜层色泽和湿热环境的耐蚀实验证明:镀锌层低铬军绿钝化膜比中铬钝化膜的胞状结构细小致密耐蚀性较高,并且低铬钝化的成膜过程不呈线性关系而是分为两个不同的阶段。
短句来源
  相似匹配句对
     Low and N.
     Low和N .
短句来源
     MADIFYING ON LOW CHROMIUM WHITE CASTIRON
     低铬白口铸铁的变质处理
短句来源
     Low-chromium Cast Alloy Iron
     低铬合金铸铁在造纸机烘缸上的应用
短句来源
     Practice on Low Chromium Coloured Passivation of Zinc Coating
     锌镀层低铬彩钝化实践
短句来源
     Chromium and Health
     铬与健康
短句来源
查询“low chromium green black passivation”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


Through SEM test, colour observation and corrosion resistance measurement in humid hot environment of passivation film on Zinc coating it is shown that structure of low chromium green black passivation film is finer than that of medium chromium green black passivation film. The corrosion resistance of low chromium passivation film is higher than that of medium chromium passivation film. The process of film formation...

Through SEM test, colour observation and corrosion resistance measurement in humid hot environment of passivation film on Zinc coating it is shown that structure of low chromium green black passivation film is finer than that of medium chromium green black passivation film. The corrosion resistance of low chromium passivation film is higher than that of medium chromium passivation film. The process of film formation is not linear relation but divided into two different stages.

经SEM、钝化膜层色泽和湿热环境的耐蚀实验证明:镀锌层低铬军绿钝化膜比中铬钝化膜的胞状结构细小致密耐蚀性较高,并且低铬钝化的成膜过程不呈线性关系而是分为两个不同的阶段。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关low chromium green black passivation的内容
在知识搜索中查有关low chromium green black passivation的内容
在数字搜索中查有关low chromium green black passivation的内容
在概念知识元中查有关low chromium green black passivation的内容
在学术趋势中查有关low chromium green black passivation的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社