aluminium-bearing steel
相关语句
  含铝钢
     The character and forming mechanism of ferrite-band structure was researched,in aluminium-bearing steel,08Cr2AlMo pipe welded joints.
     采用不同热处理工艺,研究了含铝钢08Cr2AlMo钢管熔焊接头中铁素体带形态与机理。
短句来源
     Key role of temperature on forming ferrite-band structure in welded joints aluminium-bearing steel
     温度对含铝钢熔焊接头中形成铁素体带的决定作用
短句来源
     Results show:temperature play the key role on the forming of ferrite-band structure in aluminium-bearing steel joints,welding with dissimilar weld material.
     研究发现:含铝钢异种焊材熔焊接头铁素体带形成过程中,温度起着决定作用。
短句来源
  相似匹配句对
     Production and Development of Bearing Steel
     轴承钢的生产与发展
短句来源
     -steel,s.
     -钢,Ti-S.
短句来源
     Superplasticity of Ball Bearing Steel
     GCr 15轴承钢的超塑性
短句来源
     Study on Aluminium-steel Bimetal Castings
     铝─钢双金属复合铸件研制
短句来源
     STUDY ON THE CRACK OF CAST-STEEL BEARING
     铸钢轴承座裂纹问题的研究
查询“aluminium-bearing steel”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


Aluminium-bearing steel had strong corrosive-resistant capability and had been applied widely to petro-chemical industry recent years.But carbonmigration in welded joints restricted its application.The carbon migration always causes the forming of ferrite band structure.08Cr2AlMo steel pipe welded joints were aselected as the object of research.The phase-transformation temperature of this steel was determinded.By means of the individual heat-treatment,obvious carbon depleted/enriched zone were...

Aluminium-bearing steel had strong corrosive-resistant capability and had been applied widely to petro-chemical industry recent years.But carbonmigration in welded joints restricted its application.The carbon migration always causes the forming of ferrite band structure.08Cr2AlMo steel pipe welded joints were aselected as the object of research.The phase-transformation temperature of this steel was determinded.By means of the individual heat-treatment,obvious carbon depleted/enriched zone were abtained in the fusion zone of 08Cr2AlMo pipe welded joints,with dissimilar material.Meanwhile the forming temperature range of ferrite band was measured.Results showed:The crystal structure difference between base and weld metal leads to the carbon migration.Carbon atom diffuse strongly from base metal to weld metal at about 800~850℃ in these joints.Proeutectoid ferrite plays the key role in the strong carbon migration of Al-bearing steel welded joints.

初步确定了 0 8Cr2AlMo钢的相变温度。通过热处理 ,在 0 8Cr2AlMo钢管材的异种焊材熔焊接头熔合区得到明显的脱 /增碳层 ,测定了接头中铁素体带形成的温度范围。实验发现 ,先共析铁素体是含铝钢焊接接头发生强烈碳迁移的主要条件。

The character and forming mechanism of ferrite-band structure was researched,in aluminium-bearing steel,08Cr2AlMo pipe welded joints.Results show:temperature play the key role on the forming of ferrite-band structure in aluminium-bearing steel joints,welding with dissimilar weld material.Under the experimental condition,it was at about 800℃that carbon atom diffuse strongly in08Cr2AlMo welded joints.Ferrite-band structure forms at the base metal near the fusion line.Some relevant measures to retard...

The character and forming mechanism of ferrite-band structure was researched,in aluminium-bearing steel,08Cr2AlMo pipe welded joints.Results show:temperature play the key role on the forming of ferrite-band structure in aluminium-bearing steel joints,welding with dissimilar weld material.Under the experimental condition,it was at about 800℃that carbon atom diffuse strongly in08Cr2AlMo welded joints.Ferrite-band structure forms at the base metal near the fusion line.Some relevant measures to retard the ferrite-band structure were presented.

采用不同热处理工艺,研究了含铝钢08Cr2AlMo钢管熔焊接头中铁素体带形态与机理。研究发现:含铝钢异种焊材熔焊接头铁素体带形成过程中,温度起着决定作用。在试验条件下,800℃左右08Cr2AlMo熔焊接头中发生强烈C扩散,并于熔合线母材一侧形成铁素体带,提出了抑制铁素体带形成的相关措施。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关aluminium-bearing steel的内容
在知识搜索中查有关aluminium-bearing steel的内容
在数字搜索中查有关aluminium-bearing steel的内容
在概念知识元中查有关aluminium-bearing steel的内容
在学术趋势中查有关aluminium-bearing steel的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社