  树脂基体
     Analyses by SEM,XPS and EDS reveal that the froth density of PUR/GB increases,frothy diameter decreases,the interfacial adhesion between the surface of glass bead and PUR matrix is good,and glass beads disperse homogeneously in PUR matrix.
     SEM、XPS和EDS分析表明:增强泡沫塑料的泡孔密度增加、泡孔直径变小,玻璃微珠表面与树脂基体间界面粘结状况良好,玻璃微珠在树脂基体中均匀分散。
短句来源
  相似匹配句对
     Matrix Polymerization
     聚合新技术—模板(MatriX)聚合(Ⅰ)
短句来源
     Normalization of Matrix
     矩阵的正规化
短句来源
     APPLICATION OF PUR IN LARGE WAREHOUSE
     聚氨酯硬泡体材料在高大平房仓中的应用
短句来源
     At last, the tendency of PUR foam was indicated.
     指出了今后PUR泡沫塑料的发展方向。
短句来源
     Observation of PUR Tube in Clinical Use
     复尔凯胃管在临床应用中的观察
短句来源
查询“pur matrix”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


The preparation,microstructure,compressive properties and thermal stability of the glass bead reinforced rigid polyurethane foams(PUR/GB) are studied.When the content of the glass bead reaches 10%,the compressive strength and compressive modulus of PUR/GBs reach their maximum,respectively.When glass beads are pretreated with silicane coupling agent,the compressive strength and compressive modulus improve to a large extent;the onset decomposition temperature and peak temperature improve to some extent.Analyses...

The preparation,microstructure,compressive properties and thermal stability of the glass bead reinforced rigid polyurethane foams(PUR/GB) are studied.When the content of the glass bead reaches 10%,the compressive strength and compressive modulus of PUR/GBs reach their maximum,respectively.When glass beads are pretreated with silicane coupling agent,the compressive strength and compressive modulus improve to a large extent;the onset decomposition temperature and peak temperature improve to some extent.Analyses by SEM,XPS and EDS reveal that the froth density of PUR/GB increases,frothy diameter decreases,the interfacial adhesion between the surface of glass bead and PUR matrix is good,and glass beads disperse homogeneously in PUR matrix.These are the reason why compressive properties and thermal stability are enhanced largely.

研究了玻璃微珠增强硬质聚氨酯泡沫塑料的制备、微观结构、压缩性能和热稳定性。结果表明:当玻璃微珠含量为10%时,增强泡沫塑料的压缩强度和压缩模量达到最大;经过硅烷偶联剂表面处理的玻璃微珠增强的泡沫塑料的压缩强度和压缩模量提高幅度较大,起始分解温度和峰值分解温度也有一定程度的提高。SEM、XPS和EDS分析表明:增强泡沫塑料的泡孔密度增加、泡孔直径变小,玻璃微珠表面与树脂基体间界面粘结状况良好,玻璃微珠在树脂基体中均匀分散。这些因素是造成玻璃微珠增强泡沫塑料压缩性能和热稳定性具有较大改善的原因。

 
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关pur matrix的内容
在知识搜索中查有关pur matrix的内容
在数字搜索中查有关pur matrix的内容
在概念知识元中查有关pur matrix的内容
在学术趋势中查有关pur matrix的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社