  amino silicone
     The content of acylating agent was 2.6% to 3.0% (relatively to the mass of amino silicone oil), acylating reaction temperature was 50℃ to 55℃, and the acylating time was 60~90 minutes.
     酰化剂的用量2.6%~3.0%(相对于氨基硅油的质量),酰化反应温度50~55℃,酰化反应时间60~90min。
短句来源
     Analysis of Properties of Amino Silicone Oil and Its Selection
     氨基硅油性能分析及选用
短句来源
     Synthesis and Properties of Waterborne Polyurethane Modified with Amino Silicone
     氨基硅油扩链改性水性聚氨酯的合成及性能研究
短句来源
     Construction Analysis of Amino Silicone
     氨基硅油的结构分析
短句来源
     Analysis of amino silicone softeners
     氨基硅油柔软剂的分析
短句来源
更多       
  amino-silicone
     DEVELOPMENT AND APPLIED STUDY OF WATER-SOLUBLE AMINO- SILICONE OIL
     水溶性氨基硅油的研制与应用研究
短句来源
     25.8% complex emulsifying agent(relative to the mass of amino-silicone oil);
     复合乳化剂用量为25.8%(w/w)(相对于氨基硅油的质量);
短句来源
     29.7% n-butyl alcohol(relative to the mass of amino-silicone oil);
     正丁醇用量为29.7%(w/w)(相对于氨基硅油的质量);
短句来源
     pH=4.4~4.8 and the amino-silicone oil with value of 0.3.The amino-silicone microemulsion with narrow distributing size and the diameter of its size close to 100nm was finally prepared.
     pH值在4.4~4.8之间; 氨值为0.3,制得分布较窄、粒径接近100nm的氨基硅油微乳液。
短句来源
     The silicone quaternary ammonium salt based anti-bacterial finishing agent CL was synthesized with AV amino-silicone oil and alkylated reagent WL(mole ratio=1∶2) at 80℃ × 4h. The properties of the fabric treated with it were evaluated.
     AV氨基硅油与烷基化试剂WL摩尔比1∶2 ,在80℃反应4h合成有机硅季铵盐类抗菌整理剂CL,并对其整理织物性能进行测定。
短句来源
更多       
  amino-modified silicone
     APPLIED STUDY OF AMINO - MODIFIED SILICONE QUATERNARY AMMONIUM SALT ANTIMICROBIAL AGENT HK-2002
     改性氨基硅油季铵盐类抗菌卫生整理剂HK-2002的应用研究
短句来源
     Structure analysis of amino-modified silicone oil.
     氨基硅油的结构分析
短句来源
     Preparation and Application of Polyether/amino-modified Silicone
     聚醚/氨基硅油的制备及其应用
短句来源
     The result showed that the average molar mass of the amino-modified silicone oil was 1.4780×10~4 g/mol, the viscosity of kinematics was 1 398 mPa·s, the amine value was 0.2772 mmol/g, and the monomer was N-(β-aminoethyl)-3-aminopropylmethyldimethoxysilane.
     结果表明,该氨基硅油的平均摩尔质量为1·4780×104g/mol; 动力粘度为1398mPa·s;
短句来源
     Preparation process of microemulsion of reactive amino-modified silicone oil and the relationship between its structure and properties were discussed.
     讨论了反应性氨基硅油微乳液的制备工艺及其结构与性能之间的关系.
短句来源
更多       
  “氨基硅”译为未确定词的双语例句
     The optimum reaction conditions of reactivity amino-containing silicone oil were that n(WS-62M)∶ n(SG-Si 900) =1.33∶1, the mass fraction of triethylamine was 1.55%(relative to the total weight of WS-62M and SG-Si 900), the temperature was 120℃, reaction time was 10 hours, and vacuum time under the pressure of 0.01 MPa was 0.5~1 hour.
     合成氨基硅油的最佳条件为:n(WS-62M)∶n(SG-Si900)=1·33,三乙胺质量分数1·55%(相对于WS-62M和SG-Si900的总质量),反应温度120℃,反应时间10h,在0·01MPa下抽真空0·51h;
短句来源
     The aminopolysi- loxane with regular distribution of amino groups in the molecule was synthesized under the conditions that the molar ratio of WS-62M to SG-Si900 was 1.33:1,the mass ratio of triethylamine was 1.53%,reaction temperature was 120 ℃,reaction time was 10 h,and vacuum time under a pressure of 0.01 MPa was 0.5~1 h.
     氨基硅油的最佳合成条件:n(WS-62M)/n(SG-Si900)=1.33:1,ω(三乙胺)=1.53%,反应温度120℃,反应时间10 h,在0.01 MPa 条件下抽真空0.5~1h。
短句来源
     The results showed that the optimized emulsifying conditions were as follows: m(OP-10):m(Span-80)=3:2(w/w);
     结果表明,氨基硅油的最佳乳化条件为:m(OP-10):m(Span-80)=3:2(w/w);
短句来源
     Reactive aminosilicone oil, suitable for use as a fabric softener, was synthesized using α,ω-dihydroxypolydimethylsiloxane(WS-62M) and N-β-aminoethyl-γ-aminopropyltrimethoxysiloxane(SG-Si900) as raw materials and amines as catalyst by ester exchange reaction, and the optimum synthetic conditions were determined.
     以α,ω-二羟基聚二甲基硅氧烷(WS-62M)和N-β-氨乙基-γ-氨丙基三甲氧基硅烷(SG-Si900)为原料,胺为催化剂,通过酯交换反应,合成了适用于织物柔软剂的反应性氨基硅油,并确定了最佳合成条件.
短句来源
     tert. -amino groups showed ammonium value 0.6 mmol/g and whiteness 86.1% when prepd. in a reaction at 110~160 ℃ for 6 h in the presence of catalyst at 1×10-4~3 ×10-4(based on monomer wt).
     结果表明:在催化剂用量1×10-4~3×10-4(对单体质量)、反应温度110~160℃、反应时间6h条件下,得到含叔胺的吗啉型氨基硅油的氨值0.6mmol/g,白度86.1%.
短句来源
更多       
查询“氨基硅”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


1, 2-Bis (dialkylchlorosilyl) ethane reacted with diethylamine to give 1, 2-bis (dialkyldiethylaminosilyl) ethane in 60~70% yields. By the reaction of 1, 2-bis (dialkylchlorosilyl) ethane with ammonia and ethylamine respectively, a series of novel five-membered heterocyclic silicon-nitrogen compounds were prepared in 65~70% yields, and the reaction of 1-(diethyl-chlorosilyl)-2-(ethyldichlorosilyl) ethane with ammonia yielded two fivemembered heterocyclic compounds by monomolecular and bimolecular ammonolysis,...

1, 2-Bis (dialkylchlorosilyl) ethane reacted with diethylamine to give 1, 2-bis (dialkyldiethylaminosilyl) ethane in 60~70% yields. By the reaction of 1, 2-bis (dialkylchlorosilyl) ethane with ammonia and ethylamine respectively, a series of novel five-membered heterocyclic silicon-nitrogen compounds were prepared in 65~70% yields, and the reaction of 1-(diethyl-chlorosilyl)-2-(ethyldichlorosilyl) ethane with ammonia yielded two fivemembered heterocyclic compounds by monomolecular and bimolecular ammonolysis, while with ethylamine only the former was isolated.

1,2-双(二烷基氯硅基)乙烷与二乙胺反应给出1,2-双(二烷基二乙氨基硅基)乙烷,产率60~70%,它们分别与氮及乙胺反应时,均形成五元杂环硅氮化合物,2,5-二硅-1-氮环戊烷产率65~70%、1-(二乙基氯硅基)-2-(乙基二氯硅基)乙烷与氯反应时,分离到了两种具有五元杂环的单分子和双分子氨化产物,但与乙胺反应时只分离到前一种产物。

Chioromethyltrie thoxylsilane has prepared by methyltrichlorosilane. The reaction of this compound with 2- ( 2-aminoethylamino ) ethylamine give 1-(2-(2-aminoethylamino) ethylamino) methyltriethoxy lsilane. It can accelerate the vulcanization of room temperature vulcanizing rubbers, It with methyltriethoxylsilane and tetraethyl silicate cohydrolyze to give a silicone resin.Organosilicon immobilized trypsin with biologic activity was synthesized in the presence of dicyclhoexylcarbodimide by fixing trypsin to...

Chioromethyltrie thoxylsilane has prepared by methyltrichlorosilane. The reaction of this compound with 2- ( 2-aminoethylamino ) ethylamine give 1-(2-(2-aminoethylamino) ethylamino) methyltriethoxy lsilane. It can accelerate the vulcanization of room temperature vulcanizing rubbers, It with methyltriethoxylsilane and tetraethyl silicate cohydrolyze to give a silicone resin.Organosilicon immobilized trypsin with biologic activity was synthesized in the presence of dicyclhoexylcarbodimide by fixing trypsin to these resin and determined by means of optimal temperature (50℃) and pH (PH=8.5).

本文以甲基三氯硅烷为原料,经氯化、乙酯化后得氯甲基三乙氧基硅烷,再与二乙烯三胺反应,制得了α—二乙烯三胺甲基三乙氧基硅烷(简称化合物Ⅰ)。化合物Ⅰ能加速室温硅橡胶硫化;用化合物Ⅰ制得的氨基硅树脂通过N,N’-二环巳基羰二亚胺(简称D、C.C.I)与胰酶偶联成具有生物活性的有机硅固胰酶衍生物Ⅱ,并测定了最适pH和最适温度.

The aminomodified silicone softener UE-875 is prepared through micro-emulsification technique. The advantages of this product include smaller droplet size and satisfactory stability. Its application on linen,cotton,rayon fabric is presented also.

变性氨基硅柔软剂UE—875采用微乳技术乳化而成,产品具有液态粒径小、性能稳定等优点。文章介绍了该柔软剂的性能及在麻、棉、人棉等织物上的应用情况。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关氨基硅的内容
在知识搜索中查有关氨基硅的内容
在数字搜索中查有关氨基硅的内容
在概念知识元中查有关氨基硅的内容
在学术趋势中查有关氨基硅的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社