亚稳
相关语句
  metastable
     Metastable Structure of Soft Magnetic Fe_(77-x)Ni_xCu_1Nb_2P_(14)B_6 Nanometer Polycrystals Induced by Mechanical Alloying
     纳米晶Fe_(77-x)Ni_xCu_1Nb_2P_(14)B_6软磁材料的亚稳结构
短句来源
     had no significant extension, and the metastable extensive solid solubilities of Sm, Eu, Gd, Tb, Dy, Er, Yb in Cu were determined as 0.95, 0.50, 1.2, 0.75, 1.0, 0.90, 1.0at% respectively.
     Sm,Eu,Gd,Tb,Dy,Er和Yb的亚稳扩展固溶度(at.%)分别为0.95,0.50,1.2,0.75,1.0,0.90,1.0。
短句来源
     The results show that for (Nd 0.4 Pr 0.6 ) 8.5 Fe 85.5 B6 ribbons, the metastable (Nd,Pr)3Fe 62 B 14 precipitates after the initial crystallization of α-Fe and decomposes into the final mixture of (Nd,Pr)2Fe 14 B and α-Fe.
     结果表明:(Nd0.4Pr0.6)8.5Fe85.5B6合金非晶晶化时,在α-Fe相初始晶化后,出现了(Nd,Pr)3Fe62B14亚稳相,最终亚稳相分解形成(Nd,Pr)2Fe14B和α-Fe两相组织;
短句来源
     Energy Band Structure of Metastable Semiconductor (GaAs)_(1-x)(Ge_2)_x
     亚稳半导体(GaAs)_(1-x)(Ge_2)_x的能带结构
短句来源
     ULTRASONIC STUDY OF THE METASTABLE CRYSTAL R-Li_2Ti_3O_7
     亚稳相晶体R-Li_2Ti_3O_7的超声研究
短句来源
更多       
  metastable state
     The results show that metastable state compound Bi2SiO5 resulting from solid-state reactions is changed by temperature and time in law.
     结果表明:亚稳化合物Bi2SiO5在固相反应时产生,并随温度及保温时间按一定规律变化。
短句来源
     The diffraction of metastable state compound Bi2SiO5 got from solid-state reactions is weaker as the reaction went on.
     在固相反应过程中生成的亚稳相Bi2SiO5随着反应时间延长衍射峰减弱。
短句来源
     STABLE CONDITION FOR THE THEMODYNAMIC EQUILIBRIUM AND METASTABLE STATE
     热力学平衡的稳定条件和亚稳状态
短句来源
     Silicon monoxide can easily decompose in appropriate hydrothermal system as chemical bonds between molecules are at metastable state when in high temperature and pressure.
     在高温高压下分子间的化学键处于亚稳定态,所以SiO在适当的水热体系中易发生分解与歧化反应,所生成的氧与硅片表面的硅发生化合从而可以对硅片表面进行刻蚀。
短句来源
     The micro morphology and element component were observed and analyzed by SEM and EDS. The TEM observation results show that the tantalum powder has twin crystal structure of metastable state. The major impurity elements is oxygen.
     通过SEM与EDS进行了形貌观察和成分分析,并对样品进行了TEM观察,结果表明电容器级钽粉为孪晶亚稳结构,主要杂质元素为氧。
短句来源
更多       
  metastable intermediate
     A metastable intermediate phase with hexagonal lattice structure, Ag_3 Gd, was tound in rapidly-solidified Ag—Gd alloys.
     在快速凝固合金中形成Ag_3Gd六方结构亚稳相。
短句来源
  “亚稳”译为未确定词的双语例句
     Studies on the Resistance of Annealed Fe_(80) Cu_(20) Alloy
     经热处理的Fe_(80)Cu_(20)亚稳合金的电阻特性研究
短句来源
     PHASE FORMATION IN DROP TUBE PROCESSING FROM UNDERCOOLED Pd_(77.5)Au_6Si_(16.5) MELT
     落管中Pd_(77.5)Au_6Si_(16.5)合金的固化动力学亚稳相的形成
短句来源
     The Ni-P,Ni-W-P deposits after heat-treated at 300,400,525,600℃for 1 hour turns into the Ni_3P and Ni phases,without the precipitation of intermediate phases.
     300、400、525和600℃热处理1h后,Ni-P、Ni-W-P镀层析出Ni_3P和Ni晶体,没有其它亚稳相析出;
短句来源
     Microstructure and Mechanical Properties of the Deformed Austenitic Steel 2Cr13Ni4Mn9
     2Cr13Ni4Mn9亚稳奥氏体不锈钢冷变形状态下的组织与力学性能
短句来源
     The phase transition of Fe 3B to Fe 2B in a crystallization of an amorphous (Fe 0.99 Mo 0.01 ) 78 Si 9B 13 alloys was experimentally studied in the temperature 600-930K under pressure of 2-8GPa,the change relation of phase transition temperature with pressure was determinated.
     在 2— 8GPa压力和 60 0— 930K温度的范围内 ,对非晶 (Fe0 .99Mo0 .0 1) 78Si9B13 晶化过程中亚稳Fe3B到Fe2 B的相变进行了实验研究 ,并确定了其转变温度随压力变化的关系
短句来源
更多       
查询“亚稳”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
为了更好的帮助您理解掌握查询词或其译词在地道英语中的实际用法,我们为您准备了出自英文原文的大量英语例句,供您参考。
  metastable
Results show that there were lots of Cu atom clusters in the ferrite matrix during solid solution and initial aging stage, and Cu-rich metastable Fe-Cu particles precipitate subsequently at the aging hardness peak.
      
There are also concentration ranges where the films either rupture or are metastable (quasi-equilibrium).
      
The CTAB concentration ranges, which provide the formation of unstable (rupturing and metastable) and stable films, are different for symmetric (foam) and asymmetric (wetting) thin liquid films.
      
Statistics of the Nucleation Process under the Conditions of Gradual Creation of the Metastable State in Vapor
      
Primary thick films are disclosed to be metastable.
      
更多          
  metastable state
Statistics of the Nucleation Process under the Conditions of Gradual Creation of the Metastable State in Vapor
      
A metastable state of clusters is achieved at i >amp;gt; 9.
      
The most important parameters characterizing emission from the 4F3/2metastable state of neodymium ions are obtained by analyzing the optical spectra of rare-earth ions in terms of the Judd-Ofelt theory.
      
According to one of the models, it is assumed that an instantaneous separation into phases occurs if the parameters of metal have reached values corresponding to the binodal; in the other model, the existence of a metastable state is allowed.
      
Most likely, SAFR reflects the share of cardiomyocytes in the metastable state in the total number of the cells affected by short-term ischemia, and SDFR may be an index of the time of the change in the metastable state.
      
更多          
  metastable intermediate
In the Cs2O-BaO-TiO2(ZrO2) system, the BaTi5O11 metastable intermediate phase is formed at the first stage of the solid-phase interaction.
      
The results show that a metastable intermediate phase Nd8Fe27B24 prior to α-Fe and Nd2Fe14B phases is crystallized as the amorphous Nd3.6Pr5.4Fe83Co3B5 is heated to 1 223 K.
      
An alternative route, the photoinduced charge transfer process involving local excitations to form metastable intermediate states, is discussed.
      
We study the influence of a metastable intermediate phase on the nucleation of the nematic.
      
Under non-equilibrium conditions the transformation takes place via a modulated structure which on annealing, coarsens to produce an apparently continuous sequence of metastable intermediateΔ values.
      
更多          


X 射线无定形的氢氧化铝同溶液中氯化锂的作用是固液异相反应.其产物中的主要物相为 LiCl·2Al(OH)_3·nH_2O.在 Li~+、Al~(3+)‖Cl~-、OH~-—H_2O 四元交互系中,60℃时该化合物为稳定化合物.而2LiCl·5[Al(OH)_(2.83)·Cl_(0.17)]·mH_2O 为一亚稳化合物.

The pseudo-ternary system SrNb206-NaNbO3-LiNbO2 has been investigated by means of DTA, heat treatment and X-ray diffraction techniques. It has been found that at room temperature Sr2Na(NbO3)5(S2N) is a metastable intermediate compound which has a tetragonal tungsten-bronze structure with a=12.36 A, c=3.906A. LiNbO3 can be dissolved in S2N up to a limit about 10 mol% ; and in the range of 5-10mol% of LiNbO3, the S2N phase is distorted into S2N', which belongs to the orthorhombic system and is also a metastable...

The pseudo-ternary system SrNb206-NaNbO3-LiNbO2 has been investigated by means of DTA, heat treatment and X-ray diffraction techniques. It has been found that at room temperature Sr2Na(NbO3)5(S2N) is a metastable intermediate compound which has a tetragonal tungsten-bronze structure with a=12.36 A, c=3.906A. LiNbO3 can be dissolved in S2N up to a limit about 10 mol% ; and in the range of 5-10mol% of LiNbO3, the S2N phase is distorted into S2N', which belongs to the orthorhombic system and is also a metastable phase. After long time annealing at 900-1100℃, the metastable phases S2N, S2N' will decompose into a mixture of SrNb2O6 and a phase of solid solution based on NaNbO3. The phase diagram of the corresponding binary systems and the isothermal section of the pseudo-ternary system have been established.

本文用X射线衍射、热处理及差热分析等方法测定了SrNb_2O_6-NaNbO_3-LiNbO_3赝三元系的室温截面及相应的SrNb_2O_6-NaNbO_3,SrNb_2O_6-LiNbO_3和NaNbO_3-LiNbO_3等三个赝二元系相图;粗略地研究了Sr_(0.42)Na_(0.16)NbO_3-LiNbO_3系的纵截面;含5mol%LiNbO_3及10mol%LiNbO_3的SrNb_2O_6-NaNbO_3的纵截面。确定了室温Sr_2Na(NbO_3)_5(以下略为S_2N)相为四方钨青铜结构。其点阵常数为a=12.36,c=3.906.LiNbO_3在S_2N相内的溶解度可达~10mol%,当LiNbO_3含量超过5mol%时,S_2N相畸变为S_2N相。S_2N相为正交晶系。实验确定室温S_2N(S_2N)相系亚稳相。在900-1100℃长时间退火即分解为SrNb_2O_6和以NaNbO_3为基的固溶体的混合物。

Strontium sodium lithium niobate (SNLN) single crystal possesses good electro-optical properties, but at room temperature only its metastable phase can be obtained. An eutectoidal decomposition will take place when the grown crystal is cooled slowly across the eutectoid horizontal which is about 1200℃. Single crystal up to 10 mm diameter and 15 mm in length were grown by the Czochralski method. Large temperature gradient is adopted during the growth period. The grown crystal is cooled at a higher cooling rate...

Strontium sodium lithium niobate (SNLN) single crystal possesses good electro-optical properties, but at room temperature only its metastable phase can be obtained. An eutectoidal decomposition will take place when the grown crystal is cooled slowly across the eutectoid horizontal which is about 1200℃. Single crystal up to 10 mm diameter and 15 mm in length were grown by the Czochralski method. Large temperature gradient is adopted during the growth period. The grown crystal is cooled at a higher cooling rate acress the eutectoid horizontal to avoid decomposition. The major problems in the process of growth and cause of crystal cracking are discussed.

铌酸锶钠锂单晶具有优良的电光性能,但它在室温下为亚稳相。生长的晶体降温至1200℃以下要通过共析反应区。我们用提拉法采取大温度梯度生长,在共析反应区较快速降温避免分解等措施,获得最大尺寸为直径10mm,长15mm的单晶。文中讨论了引起开裂的原因及生长过程中遇到的主要问题。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关亚稳的内容
在知识搜索中查有关亚稳的内容
在数字搜索中查有关亚稳的内容
在概念知识元中查有关亚稳的内容
在学术趋势中查有关亚稳的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社