     Based on 40Si2MnV,32 mm high-strength reinforced bar for prestressing concrete which can meet the standard ASTM A722-95 has been developed by appropriate microalloying element design,temperature-controlled rolling and residual heat treatment. The basic microstructure is of ferrite-pearlite.
     以40Si2MnV为基本钢种,进行微合金化处理,并采用控温轧制和轧后穿水冷却工艺,研制开发出了满足ASTM A722-95标准的φ32mm高强度精轧螺纹钢筋,钢筋的基本组织为铁素体+珠光体。
     42CrMoVNb steel with ultrafine prior austenite grain, its size as fine as 2 μm, was
     对于微合金化处理的42CrMoVNb钢,通过快速循环热处理的方法获得最小2μm的超细奥氏体晶粒,采用缺口拉伸延迟断裂实验研究了超细晶粒试样的延迟断裂行为.
短句来源
     Investigation on Microalloying of Ultra-low-carbon High Strength BH Sheet Steel
     超低碳高强BH钢板的微合金化处理研究
短句来源
     Proper micro-alloying has been made on the Al-Si alloy on the basis of the effective alloy refinement.
     在有效的熔体处理基础上 ,对Al-Si合金进行适当的微合金化处理 ,可明显提高Al-Si合金的力学性能。
短句来源
     After niobium microalloying for high carbon steel,the mechanical properties of wire rods was improved.
     铌微合金化处理后高碳钢线材的力学性能得到了改善。
短句来源
更多       
  相似匹配句对
     Comprehensive Evaluation for Heat-treated State of Microalloying Cast Steel
     微合金化铸钢处理状态的综合评判
短句来源
     IN SMALL AMOUNTS ALLOYING AND DISPERSION STRENTHENING TREATMENT OF HIGH MANGANESE STEEL
     高锰钢微合金化及弥散强化处理
短句来源
     TREATMENT OF ION EXCHANGE RESINS
     离子交换树脂的处理
短句来源
     Natural Language Processing
     自然语言处理
短句来源
查询“微合金化处理”译词为用户自定义的双语例句

    我想查看译文中含有:的双语例句
例句
没有找到相关例句


This paper describes the solution of fracture problems existed in the heavy 70Mn Cast steel rolls by rare earth metals modification and V, Ti microalloying. As a result, the fracture-resistance and rolling-force of the rolls are increased.

本文针对70Mn大型铸钢轧辊的断裂问题,应用稀土变质处理,钒钛微合金化处理,结果提高了轧辊的抗裂性和轧制能力。

he influence of multi-microalloy on the micro structure.mechanical properties and the wear resistance of the RE low chromium white cast iron is tesearched in this paper.he re-sults show that by microalloying the structureis obviously refined,the hardness is increased and the dynamic fracture toughness and the wear resistance are improved by 47.2%and 80.2%separately,The simulation test proves that when the grinding ball made from this white cast iron is used to grindcement,its wear is the same to that of hign...

he influence of multi-microalloy on the micro structure.mechanical properties and the wear resistance of the RE low chromium white cast iron is tesearched in this paper.he re-sults show that by microalloying the structureis obviously refined,the hardness is increased and the dynamic fracture toughness and the wear resistance are improved by 47.2%and 80.2%separately,The simulation test proves that when the grinding ball made from this white cast iron is used to grindcement,its wear is the same to that of hign chromium grin ding ball.

文中详细探讨了多元微合金化对稀土低铬白口铸铁显微组织、力学性能和抗磨性的影响。结果表明:微合金化处理稀土低铬白口铸铁,组织明显细化,硬度略有提高,动态断裂韧性提高47.2%,抗磨性提高80.2%。模拟试验表明,采用多元微合金稀土低铬白口铸铁磨球磨水泥,其磨耗与高铬球相当。

The structural characteristics analysis of ELC-BH sheet steel treated by two differentmicroalloying ways has been carried out by utilizing an ODF structural analysis method. The resultsshow that the Nb treated ELC-BH sheet steel has a stronger γ fibre microstructure but weaker andincomplete a fibre microstructure in comparison with the Nb+Ti treated one,because the adding ofelement Ti in Nb + Ti treatment might be disadvantageous to the growth of {111} annealed microstructure.

采用ODF等织构分析方法对两种不同微合金化处理的ELC-BH钢板进行了织均分析。结果表明,Nb处理的ELC-BH板较Nb+Ti处理板具有较强的γ纤维织构和较弱的不完整α纤维织均,这是由于Nb+Ti处理板中Ti元素加入,对{111}退火织构发展不利作用所致。

 
<< 更多相关文摘    
图标索引 相关查询

 


 
CNKI小工具
在英文学术搜索中查有关微合金化处理的内容
在知识搜索中查有关微合金化处理的内容
在数字搜索中查有关微合金化处理的内容
在概念知识元中查有关微合金化处理的内容
在学术趋势中查有关微合金化处理的内容
 
 

CNKI主页设CNKI翻译助手为主页 | 收藏CNKI翻译助手 | 广告服务 | 英文学术搜索
版权图标  2008 CNKI-中国知网
京ICP证040431号 互联网出版许可证 新出网证(京)字008号
北京市公安局海淀分局 备案号:110 1081725
版权图标 2008中国知网(cnki) 中国学术期刊(光盘版)电子杂志社